Abstract:High-strength, high-porosity and relatively low-shrinkage ZrO 2 ceramics were successfully fabricated by material extrusion 3D printing technology via optimizing CaCO 3 addition and sintering temperature. The effects of different CaCO 3 additions on the performance, phase formation, and microstructure of porous ZrO 2 ceramics sintered at different temperatures were systematically investigated and discussed. The results showed that flexural strength, porosity and shrinkage of the ZrO 2 ceramics were significantly affected by CaCO 3 addition and sintering temperature. The appropriate addition of CaCO 3 could promote sintering and phase transformation of m-ZrO 2 , increase the number and size of pores in the matrix. The corresponding flexural strength and porosity of the sintered samples increased, while the shrinkage rate decreased. The raised sintering temperature appropriately facilitated the formation of CaZrO 3 . Microstructural analysis indicated that CaZrO 3 exhibited a larger polyhedral bulk morphology, mainly distributed at the edges of pores, which could stabilize the pore structure and thicken the sintering necks, and thereby exhibiting well-balanced comprehensive performance. The ZrO 2 ceramics with high flexural strength, high porosity and relatively low shrinkage rate were achieved by adding 15 wt% CaCO 3 and sintering at 1450 °C. The resulting flexural strength and porosity were 27.33 MPa and 67.62 %, respectively, presenting an improvement of 563.35 % and 13.69 % compared to ZrO 2 ceramics without CaCO 3 . Moreover, the shrinkage rates in the X-direction (9.98 %), Y-direction (9.62 %), and Z-direction (9.94 %) significantly reduced, decreasing by 38.28 %, 38.10 %, and 41.46 %, respectively.

Preparation and property characterization of Zr-modified Si-O-C-based precursor ceramics through three-dimensional printing

Properties and ceramic transformation of Si–Zr–O–C precursor ceramics with porous structure

Fabrication of High-Performance Al2O3-ZrO2 Composite by a Novel Approach That Integrates Stereolithography-Based 3D Printing and Liquid Precursor Infiltration

R-curve of La2O3 doped Zirconia Toughened Alumina Composites Prepared via Stereolithography based 3D Printing

Preparation and stereolithography 3D printing of ultralight and ultrastrong ZrOC porous ceramics

The Rising Crack Resistance Curve Behavior and Mechanism of La2O3 Doped Zirconia Toughened Alumina Composites Prepared Via Vat Photopolymerization Based 3D Printing

The preparation of ZrO2-Al2O3 composite ceramic by SLA-3D printing and sintering processing

Preparation of complex SiOC ceramics by a novel photocurable precursor with liquid crystal display ( LCD) 3D printing technology

3D Printed Zirconia Ceramics Via Fused Deposit Modeling and Its Mechanical Properties

Preparation, characterization and coloring mechanism of 3D printed colorful ZrO 2 ceramics parts

Preparation of ZTA composite ceramics derived from sol–gel method by DIW printing

Mechanical reinforcement of 3D printed cordierite-zirconia composites

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Microstructure and mechanical properties of 3D‐printed zirconia bone scaffold: Experimental and computational analysis

Enhanced biomedical applicability of ZrO2–SiO2 ceramic composites in 3D printed bone scaffolds

Optimized preceramic polymer for 3D structured ceramics via fused deposition modeling

Preparation of Alumina-Toughened Zirconia Via 3D Printing and Liquid Precursor Infiltration: Manipulation of the Microstructure, the Mechanical Properties and the Low Temperature Aging Behavior

Preparation, Microstructure, and Properties of ZrO2(3Y)/Al2O3 Bioceramics for 3D Printing of All-ceramic Dental Implants by Vat Photopolymerization

Achieving high-strength, high-porosity and relatively low-shrinkage in extrusion-based 3D printed ZrO 2 ceramics by adjusting CaCO 3 addition and sintering temperature

Preparation of excellent performance ZTA ceramics and complex shaped components using digital light processing 3D printing technology