Abstract:Although 4Ce4YSZ has high corrosion resistance, it faces challenges concerning its sinterability and ionic conductivity. Therefore, we studied destabilization behavior caused by corrosion and oxygen vacancy ordering according to ZnO doping. Powders of (4Ce4YSZ)1−x(ZnO)x (x = 0.5, 1, 2, 4 mol%) were synthesized using the sol-gel method. With the addition of ZnO, the cubic phase increased, and secondary phases were not observed. The (111) peak showed a higher angle shift in ZnO-doped 4Ce4YSZ compared to 4Ce4YSZ, and TEM-SAED revealed a reduction in the spacing of the (011)t plane, suggesting lattice contraction due to the substitution of the smaller Zn2+ (60 Å) for Zr4+ (84 Å) in the lattice. The local atomic structure analysis was conducted using EXAFS to investigate the oxygen vacancy ordering behavior. Zr K-edge Fourier transform data revealed a decrease in the Zr-O1 peak intensity with an increasing amount of ZnO doping, indicating an increase in oxygen vacancies. The Zr-O1 peak position shifted to the right, leading to an increase in the Zr-O1 interatomic distance. In the Y K-edge Fourier transform data, the Y-O1 peak intensity did not decrease, and there was little variation in the Y-O1 interatomic distance. These results suggest that the oxygen vacancies formed due to ZnO doping are located in the neighboring oxygen shell of Zn, rather than in the neighboring oxygen shells of Y and Zr. Impedance measurements were conducted to measure the conductivity, and as the amount of ZnO doping increased, the total conductivity increased, while the activation energy decreased. The increase in oxygen vacancies by ZnO doping contributed to the enhancement of conductivity, and it is considered that these created oxygen vacancies did not interact with Zn2+ and did not form defect associations. Fluoride-based molten salts were introduced to the specimens to assess the corrosion behavior in a molten salt environment. Yttrium depletion layers (YDLs) were formed on the surfaces of all specimens due to the leaching of yttrium. However, Ce remained relatively stable at the interface according to EDS line scans, suggesting a reduction in the phase transformation (cubic, tetragonal to monoclinic) typically associated with yttrium leaching in YSZ.

On the role of the zirconia/ceria interface in the degradation of solid oxide electrolysis cells

The oxygen partial pressure in solid oxide electrolysis cells with two layer electrolytes

Interdiffusion between gadolinia doped ceria and yttria stabilized zirconia in solid oxide fuel cells: Experimental investigation and kinetic modeling

Lower Down Both Ohmic and Cathode Polarization Resistances of Solid Oxide Fuel Cell Via Hydrothermal Modified Gadolinia Doped Ceria Barrier Layer

Performance Analysis of a Metal-Supported Intermediate-Temperature Solid Oxide Electrolysis Cell

Impact of Sr-Containing Secondary Phases on Oxide Conductivity in Solid-Oxide Electrolyzer Cells

Degradation Issues in Solid Oxide Electrolysers

High performance and stability of nanocomposite oxygen electrode for solid oxide cells

Impedance analysis of thin YSZ electrolyte for low-temperature solid oxide fuel cells

Performance and Stability Analysis of SOFC Containing Thin and Dense Gadolinium-Doped Ceria Interlayer Sintered at Low Temperature

Enhancement of the Cathode/electrolyte Interface by a Sintering-Active Barrier Layer for Solid Oxide Fuel Cells

Enhanced Cathode/Electrolyte Interface by a Nano-Modified Barrier Layer for Solid Oxide Fuel Cells

Preparation, Evaluation, and Application of SUS430/441 Interconnect with Mn-Co Coating in Solid Oxide Fuel Cells

Electrical and Hydrogen Reduction Enhances Kinetics in Doped Zirconia and Ceria: II. Mapping Electrode Polarization and Vacancy Condensation in YSZ

Construction and Scale-Up of High Performing SOFC with Enhanced GdxCe1−xO2−δ Barrier Layer Self-Crystallization and Defect-Free GDC-YSZ Interface

The oxygen partial pressure in solid oxide electrolysis cells with multilayer electrolytes

Effect of Grain Boundary Diffusion on Electrolyte Stability in Direct Carbon Fuel Cells with Antimony Anodes

Performance of a double-layer CGO/YSZ electrolyte for solid oxide fuel cells

Interfacial energy barrier: A crucial factor affecting cathodic polarization resistance of solid oxide fuel cells

Oxygen Vacancy Ordering and Molten Salt Corrosion Behavior of ZnO-Doped CeYSZ for Solid Oxide Membranes

In Situ Densification of Gadolinium-Doped Ceria Interlayer by Infiltration Process in SOFC