Microstructure and mechanical properties of MoNbW(TaC)x composites

Guoqiang Luo,Shijing Jiang,Qinqin Wei,Kejia Kang,Yichang Qian,Jian Zhang,Yi Sun,Qiang Shen

DOI: https://doi.org/10.1016/j.ijrmhm.2021.105574

IF: 4.804

2021-09-01

International Journal of Refractory Metals and Hard Materials

Abstract:In this study, novel MoNbW(TaC)x composites with eutectic-like structures were firstly prepared by arc melting. The composites consisted of body-centered cubic (BCC) structured high entropy alloy (HEA) and face-centered cubic (FCC) structured carbide (Mo, Nb, Ta, W)C. During the solidification, eutectic reaction occurred in the composites to form eutectic structures of BCC phase and subcarbide (Mo, Nb, Ta, W)2C, and then the subcarbide decomposed into eutectoid structures of BCC phase and carbide (Mo, Nb, Ta, W)C. So the composites exhibited a new eutectic-like structures composed of BCC phase and fine nanoscale eutectoid structures. The MoNbW(TaC)0.9 composite with a fully eutectic-like microstructure exhibited ultimate compressive strength of 2779 ± 37 MPa. The MoNbW(TaC)0.5 composite showed the highest plastic strain of 10.80 ± 0.56% with the compressive strength of 1803 ± 33 MPa. The strengthening mechanisms of the composites are mainly the second phase strengthening and the grain refinement.

materials science, multidisciplinary,metallurgy & metallurgical engineering