Abstract:Mg-Gd system alloys have been widely studied because they are applied in automotive, weaponry and aerospace applications and have a wide range of application scenarios due to the excellent strength and heat resistance properties. This work aims to systematically investigate the microstructure and high temperature mechanical properties of Mg-10Gd-3Y-xNd-0.5Zr alloy, and found that the microstructure of Mg-10Gd-3Y-0.5Zr alloy was mainly composed of a-Mg matrix, Mg5(Gd, Y) phase and Mg24(Y, Gd)5 phase. In which Nd element plays a role in the alloy to promote the precipitation phase precipitation and form the new phase Mg41Nd5, and the appropriate amount of Nd can refine the grain size. Moreover, Mg-10Gd-3Y-xNd-0.5Zr alloy has excellent mechanical properties in room and high temperature, with ultimate tensile strengths above 280 MPa at 200 degrees C-300 degrees C, 309 MPa at 250 degrees C, and especially at 350 degrees C, the tensile strength is still up to 195 MPa. The main strengthening phases are p" phase, p' phase and 18-LPSO (Long-period stacking ordered) phase. The Mg-10Gd-3Y-2Nd-0.5Zr alloy has excellent high temperature creep resistance at (200 degrees C-300 degrees C)/(50-90 MPa). When creeping at 200 degrees C, p' phase is completely transformed into p" phase. After creeping at 250 degrees C, p' phase is transformed into p phase. After creeping at 300 degrees C, p phase grows significantly. Meanwhile, when the creep temperature and stress increase, the creep mechanism gradually changes from diffusion and grain boundary sliding mechanism to dislocation slip and dislocation climbing mechanism. (c) 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Kinetics of Aging and Changes in the Mechanical Properties of Mg – Y – Nd – Gd – Zn – Zr Cast Magnesium Alloy During Overburning

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Elevated-Temperature Mechanical Behavior of Peak-Aged Mg–10Gd–3Y–0.4Zr Alloy

Age Hardening Characteristics and Mechanical Properties of Mg-3.5dy-4.0gd-3.1nd-0.4zr Alloy

Effect of Aging Temperature on Microstructure and Mechanical Properties of Mg-12Gd-3Y-1Sm-0.5Zr Alloy

Effects of Ageing Treatment on Microstructures and Properties of Mg–Gd–Y–Zr Alloys with and Without Zn Additions

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

A Preliminary Study on the Effects of Aging Temperature on the Microstructure and Mechanical Properties of As-Extruded Mg-12Gd-4Y-1Zn Magnesium Alloy

Effect of Aging Temperature on Microstructure and Mechanical Properties of AZ81-4%Gd Magnesium Alloy

Aging characteristics and mechanical properties of cast and wrought MG-11GD-2ND-0.5ZR alloys

Microstructure Evolution in a Mg–15Gd–0.5Zr (wt.%) Alloy During Isothermal Aging at 250°C

Effects of Gadolinium on Aging Behavior and Mechanical Properties of Mg-5Y-3Nd-Zr Alloy

Influence of Heat Treatment on Microstructures and Mechanical Properties of Gravity Cast Mg–4.2Zn–1.5RE–0.7Zr Magnesium Alloy

Synergic Effects of Gd and Y Contents on the Age-Hardening Response and Elevated-Temperature Mechanical Properties of Extruded Mg–Gd(-Y)-Zn-Mn Alloys

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Effects of Heat Treatments on the Microstructures and Mechanical Properties of Mg–3Nd–0.2Zn–0.4Zr (wt.%) Alloy

Microstructure and high temperature mechanical properties of the Mg-Gd-Y(-Nd)-Zr alloy

Microstructure and Age-Hardening of As-Cast Mg-5Zn-0.6Zr-1RE-2Y Magnesium Alloy Aged at Low Temperature

Effects of Aging Treatment on the High-Temperature Mechanical Behavior of Laser-Welded High-Strength Mg-Gd-Y Alloy

Characterization and Strengthening Effect of Precipitate Microstructure in Mg-3nd-3gd-0.2zn-0.5zr Alloy Aged at 225 °C