Investigation on effects of nano-reinforcement on the mechanical properties, fatigue, and microstructural analysis of dissimilar AA6061- Mg AZ31B weld joints

Chakravarthi Gurijala,Ramadoss R,K GIRIDHARAN

DOI: https://doi.org/10.1088/1402-4896/ad804e

2024-09-28

Physica Scripta

Abstract:In this research work challenge can be answered by incorporating nanomaterials into the weld zone. Mechanical and metallurgical aspects of Friction Stir Welded (FSW) butt joints made of AA6061 aluminum and Mg AZ31B alloys have been examined in this work, both with and without the use of naturally derived biochar nanoparticles. The biochar particle was extracted from the rice husk. Throughout the whole weld joint manufacturing process, a tool with a rotational speed of 1400 rpm, a welding speed of 40 mm/min, and a tapered pin profiled tool was employed. During the joint fabrication process, the constant axial load of 7 kN, plunge depth of 0.2 mm, and the constant dwell time of 0.3s were also maintained. To improve the mechanical attributes of the weld joints, different Wt % of biochar such as 1%, 2%, and 3% were applied at the interface region of the weld joints. The results revealed that the percentage of reinforced nanomaterials plays a significant effect in improving the weld joint qualities. The testing results of reinforced friction stir welded joint qualities were compared to those simple friction stir welded joints made with and without adding the nanoparticles. The best results were obtained when a 2 Wt % of biochar particles were added to the weld interface region. The presence of biochar nanoparticles, in addition to their contribution to increased grain refinement in the weld nugget region, was also seen in the region. The presence of 2 Wt % biochar particles in the weld nugget region resulted in a considerable increase in the mechanical characteristics of the weld connections. Is a resulted of the weld nugget the ultimate tensile strength, hardness, and yield strength are 197 MPa, 173HV, 163 MPa Overall, when compared to the qualities of the base material and plain weld joints.

physics, multidisciplinary