Abstract:It is expected that the demand for Metal Matrix Composite (MMCs) will increase in these applications in the aerospace and automotive industries sectors, strengthened AMC has different advantages over monolithic aluminium alloy as it has characteristics between matrix metal and reinforcement particles. However, adequate joining technique, which is important for structural materials, has not been established for (MMCs) yet. Conventional fusion welding is difficult because of the irregular redistribution or reinforcement particles. Also, the reaction between reinforcement particles and aluminium matrix as weld defects such as porosity in the fusion zone make fusion welding more difficult. The aim of this work was to show friction stir welding (FSW) feasibility for entering Al 6061/5 to Al 6061/18 wt. % SiCp composites has been produced by using stir casting technique. SiCp is added as reinforcement in to Aluminium alloy (Al 6061) for preparing metal matrix composite. This method is less expensive and very effective. Different rotational speeds,1000 and 1800 rpm and traverse speed 10 mm \ min was examined. Specimen composite plates having thick 10 mm were FS welded successfully. A high-speed steel (HSS) cylindrical instrument with conical pin form was used for FSW. The outcome revealed that the ultimate tensile strength of the welded joint (Al 6061/18 wt. %) was 195 MPa at rotation speed 1800 rpm, the outcome revealed that the ultimate tensile strength of the welded joint (Al 6061/18 wt.%) was 165 MPa at rotation speed 1000 rpm, that was very near to the composite matrix as-cast strength. The research of microstructure showed the reason for increased joint strength and microhardness. The microstructural study showed the reason (4 %) for higher joint strength and microhardness. due to Significant of SiCp close to the boundary of the dynamically recrystallized and thermo mechanically affected zone (TMAZ) was observed through rotation speed 1800 rpm. The friction stir welded ultimate tensile strength Decreases as the volume fraction increases of SiCp (18 wt.%).

Influence of SiC Nanoparticle Reinforcement on FSS Welded 6061-T6 Aluminum Alloy

Effect of SiC/Si3N4 micro-reinforcement on mechanical and wear properties of friction stir welded AA6061-T6 aluminum alloy

In-situ nanocomposite in friction stir welding of 6061-T6 aluminum alloy to AZ31 magnesium alloy

Nanoparticles Addition in AA2024 Aluminum/Pure Copper Plate: FSSW Approach, Microstructure Evolution, Texture Study, and Mechanical Properties

Microstructure and Mechanical Properties of Friction Stir Welded SiC/TiB2 Reinforced Aluminum Hybrid Composites

Investigation of SiC Nanoparticle Size and Distribution Effects on Microstructure and Mechanical Properties of Al/SiC/Cu Composite during the FSSW Process: Experimental and Simulation

An appraisal of characteristic mechanical properties and microstructure of friction stir welding for Aluminium 6061 alloy – Silicon Carbide (SiCp) metal matrix composite

Friction Stir Weld of AZ91 Magnesium Alloy With and Without Nano-SiC Particle

Experimental Review on Friction Stir Welding of Aluminium Alloys with Nanoparticles

Depriving friction stir weld defects in dissimilar aluminum lap joints

Effect of SiC interlayer on microstructure and joint strength of Cu-Al welds obtained using a new friction processing method

The effect of rotational speed and dwell time on Al/SiC/Cu composite made by friction stir spot welding

Impact of friction stir welding parameters and Al2TiO5 reinforcement on the mechanical, wear, and corrosion performance of dissimilar welded aluminium composite joints

Consequence of reinforced SiC particles on microstructural and mechanical properties of AA6061 surface composites by multi-pass FSP

Parametric effect on microstructure evolution, grain size and mechanical behaviour of friction stir butt welding of AA6061-T6 alloy

Dissimilar friction stir welding of 7075 aluminum alloy to AZ31 magnesium alloy using SiC nanoparticles

Investigation on effects of nano-reinforcement on the mechanical properties, fatigue, and microstructural analysis of dissimilar AA6061- Mg AZ31B weld joints

Experimental investigation of weld characteristics on submerged friction stir welded 6061-T6 aluminum alloy

Strengthening Behavior in SiC Nanowires Reinforced Pure Al Composite

The Effect of SiC Particle Addition During FSW on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Improving mechanical properties of FSWed AA6061-T6 joint by controlling microstructural changes through utilization of stationary shoulder tool in presence of Al2O3 nanoparticles and external cooling