Abstract:A comprehensive research project consisting of pilot-scale combustion testing and long-term laboratory corrosion study has been performed. A pilot-scale combustion facility was modified to enable burning of pulverized coals under the conditions typical for coal-fired utility boilers. Eight United States (U.S.) coals were selected for this investigation, with the test conditions for all coals set to have the same heat input to the combustor. In addition, the air/fuel ratio was controlled so that approximately 3% excess oxygen was attained in the combustion gas at the furnace outlet, a location equivalent to the furnace exit of commercial boilers. During each pilot-scale combustion test, extensive online measurements of the flue gas compositions were performed. In addition, deposit samples were collected at the same location for chemical analyses. This information characterized well the combustion environments adjacent to the superheaters and reheaters of utility boilers burning different U.S. coals. The gas and deposit compositions were then simulated in a series of 1000-hour laboratory corrosion tests in which the corrosion performances of different alloys were evaluated at 704oC (1300oF). Results of this laboratory study led to better understanding of the corrosion mechanisms operating on superheaters and reheaters in coal-fired boilers due to the mutual presence of sulfur and chlorine in coal. A new corrosion mechanism, i.e., “Active Sulfide-to-Oxide Corrosion Mechanism,” accounts for the rapid corrosion attack on low-alloy ferritic steels and lower-grade stainless steels resulting from the formation of iron chloride (FeCl2) vapor and associated cycling reactions. For higher alloys containing sufficient chromium, the attack is dominated by Hot Corrosion in the presence of a fused salt. In addition, two stages of the hot corrosion mechanism have been elucidated here in detail. The initiation of hot corrosion attack induced by molten sulfate may involve Stage 1 “acidic” fluxing and re-precipitation of the protective scale formed initially on the deposit-covered alloy surfaces, followed by Stage 2 Hot Corrosion dominated by “basic” fluxing and re-precipitation after the scale is locally penetrated by the fused salt.

High-temperature sulfur corrosion of iron-chromium alloys

High Temperature Oxidation of Fe-Cr Alloys in Atmospheres Containing 2.0 % SO2+5.0 % O2

Mechanisms of chromia scale failure during the course of 15–18Cr ferritic stainless steel oxidation in water vapour

Real-Time Observation of High-Temperature Gas Corrosion in Dry and Wet SO2-Containing Atmosphere

The problem of sulfur in high-temperature corrosion

The Effect of Silicon Addition on the High Temperature Oxidation of a Fe-Cr Alloy

Iron oxide fluxing and precipitation in sulphate deposits during heat-resistant alloy corrosion in simulated combustion gas

Phase Transformation Behavior Of Oxide Scale On Plain Carbon Steel Containing 0.4 Wt.% Cr During Continuous Cooling

Beyond the Sulfur Effect

High‐Temperature Oxidation of Fe–Si Alloys in Atmospheres Containing 2.0% SO2 + 5.0% O2

A Study of the Mechanism of Formation of Composite Oxide Scale on Heat-Resistant Steel 25Cr18Ni9Si2

Sulfidation behavior of an AlCoCrNiSi high‐entropy alloy

Oxidation After Breakdown of the Chromium-Rich Scale on Stainless Steels at High Temperature: Internal Oxidation

First-Principles Study of Sulfur Corrosion Mechanism at Carbon Steel Grain Boundaries

Effect of Chromium and Water Vapor of Low Carbon Steel on Oxidation Behavior at 1050 °C

Oxide scale microstructure and failure mechanism of alloy 601 under varying metal dusting conditions

Comparative Study on Oxidation Behavior of Fe-5wt% Cr Alloy in Various Mixed Atmospheres at 900–1 000 °C

Morphology and Buckling of the Oxide Scale after Fe–9Cr Steel Oxidation in Water Vapor Environment

Effect of Sulfur on Microstructures and Solidification Characteristics of a Nickel-Base Single Crystal Superalloy

High-Temperature Corrosion Mechanisms for Selected Iron and Nickel-Based Alloys Exposed to Sulfur and Chlorine-Containing Environments

Corrosion behaviour of high silicon alloys in carbon-bearing and high sulfur atmospheres