Abstract:One of the critical issues in the efficient operation of the solid oxide fuel cell (SOFC) is the interface fracture caused by the release process of the residual stress inside the sealant in the thermal cycle. The effects of sintering temperature at 700, 750, 800 and 850 °C on the residual stress caused by the crystallization process of SrO-MgO-SiO 2 glass-ceramic were investigated systematically. The structure evolution was observed using the SEM equipped with EDS, and the phase composition was detected by the XRD and Raman spectrum. The residual stress was characterized using XRD, Raman spectroscopy and nanoindentation methods. The results showed that the sintering process promoted the crystallization process. The Sr 2 MgSi 2 O 7 phase was formed at the range from 735 to 847 °C, which improved the mechanical properties and formed residual stress. The XRD and Raman peaks shifted toward the high angle, indicating that the residual compressive stress was caused by the lattice mismatch of the crystal phase. With the sintering temperature increasing from 750 to 850 °C, the residual stress values changed from − 867.472 to − 113.338 MPa in the (211) plane by the XRD method. The redshift of 901 cm −1 Raman peak indicated the residual compressive stress decreased from − 355.6 for SMS-800 to − 101.6 MPa for SMS-850. The left displacement in the nanoindentation experiment also suggested compressive stress in the SMS-750, SMS-800 and SMS-850 with a value of − 307.691, − 227.244 and − 175.161 MPa, respectively. However, a residual tensile stress existed in the SMS-700. As the sintering temperature increased, the compressive stress of SMS-850 had a decrease of 43% compared with SMS-750. The fracture toughness of SMS-850 reached the maximum of 1.12 MPa·m 1/2 due to the crystal phase increase and residual stress reduction.

Effect of holding time in brazing cooling process on creep life of the solid oxide fuel cell with bonded compliant seal

High temperature creep strength design and optimization of solid oxide fuel cell

Mismatch effect of material creep strength on creep damage and failure probability of planar solid oxide fuel cell

Study on creep damage and life prediction of the planar solid oxide fuel cell by modeling of multiphysics coupled

Effect of Sintering Temperature on the Residual Stress of SrO-MgO-SiO2 Glass-Ceramic Sealant for Solid Oxide Fuel Cells

Long-term thermo-mechanical performance evolution of a 15-cell solid oxide fuel cell stack

Effects of a cooling channel on the creep damage and failure probability of planar solid oxide fuel cells

Investigation of creep damage and failure probability in solid oxide fuel cells with different flow channel geometries

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Brazing manufacturing technology of plate-fin heat exchanger for solid oxide fuel cells

Low thermal stress and excellent gas tightness in BaO‒CaO‒Al2O3‒B2O3‒SiO2 glass‐ceramic for long‐term ITSOFC application

A review on solid oxide fuel cell durability: Latest progress, mechanisms, and study tools

The effects of thermal aging on metallic interconnects of solid oxide fuel cells

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

Influence of Post-Bond Heat Treatment on Microstructure and Creep Behavior of the Brazed Single-Crystal Nickel Superalloy

Oxidation behavior and interface diffusion of porous metal supported SOFCs with all plasma sprayed functional layers in air at 650oC

Study on expansion characteristics of Al–Al2O3 composite seals for intermediate‐temperature solid oxide fuel cell

High-Temperature Stress-Rupture Properties of a Ferritic Steel for Solid Oxide Fuel Cell Interconnect

Unravelling the oxidation behaviors of porous stainless steel 430L substrate for metal-supported solid oxide fuel cells

Creep strength and toughness synergistic strengthening mechanism investigation of the Inconel625/ BNi-2 brazed joint