Abstract:Magnesium-zinc-calcium alloys have unique advantages of being used as biomedical bone implants since their mechanical properties and biocompatibility are similar to human tissues. However, insufficient strength and poor corrosion resistance have been the major problems to stunt the application. In this paper, the changes of microstructure, mechanical properties and corrosion resistance of ternary Mg-3Zn-0.2Ca (wt.%) with different contents of Mn (0.3, 0.5, 0.7, 0.9, wt.%) are studied. With the increase of Mn content, the grain size of as-cast alloy first decreases and then increases, this indicates that the amount of Mn affects the degree of subcooling of the alloy. At the 320°C/24 h homogenizing treatment, the large and uneven dendrites are transformed into uniform equiaxed grains, the mechanical properties of alloys with different Mn contents are different on the basis of Mg-3Zn-0.2Ca (wt.%) alloy. The five alloys were extruded into bar with a diameter of 8 mm through hot-extrusion process. Quaternary Mg-3Zn-0.2Ca-XMn (X = 0.3, 0.5, 0.7, 0.9) (wt.%) alloys are investigated and the results show that 0.5 wt.% Mn alloy has the best yield tensile strength (YS) (302 MPa) and good ultimate tensile strength (UTS) (327 MPa). The reason is that the different contents of Mn restrain the dynamic recrystallization in extrusion process, which remarkedly reduced the grain size. Moreover, each alloy is investigated by electrochemical measurements at 37°C in a simulated body fluid (SBF). The electrochemical results show that the corrosion potential of Mn-contained alloys are increased compared to ternary Mg-3Zn-0.2Ca (wt.%) alloy, and 0.5 wt.% Mn-contained alloy performs the best result.

Effect of Al/Mn ratio on corrosion behavior of lean Mg-Zn-Ca-Al-Mn alloy processed by twin-roll casting

Role of alloyed Al on the microstructure and corrosion behavior of as-cast dilute Mg-2Zn- x Al-0.5Ca alloys

Effect of Mn Element Addition on the Microstructure, Mechanical Properties, and Corrosion Properties of Mg-3Zn-0.2Ca Alloy

Improved Strength and Enhanced Pitting Corrosion Resistance of Al-Mn Alloy with Zr Addition

Effect of the Zn/Mg Ratio on Microstructures, Mechanical Properties and Corrosion Performances of Al-Zn-Mg Alloys

Effect of Al on the microstructure and corrosion resistance of high-Mn steel

Enhancing mechanical properties of twin-roll cast Al–Mg–Si–Fe alloys by regulating Fe-bearing phases and macro-segregation

High corrosion resistance and weak corrosion anisotropy of an as-rolled Mg-3Al-1Zn (in wt.%) alloy with strong crystallographic texture

Effect of Zn/Mg Ratio on Microstructure and Properties of Cold Extruded Al-xZn-2.4Mg-0.84Cu-0.2Zr-0.25Ti Aluminum Alloy

Effect of Al/Mg Ratio on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

Influence of β-Mg 17 Al 12 and Al-Mn intermetallic compounds on the corrosion behaviour of cast and solution treated Mg-Al-Zn-Mn alloys

Effect of Al on the Microstructure and Mechanical Properties of Mg–Sn–Ca–Mn Wrought Alloy

Study on the microstructure and corrosion resistance of Zn-3Al-xMg alloy

Effect of Mg on the Corrosion Resistance of Hot-Dip Zn-Cu-Ti Alloy

Effect of Zn/Mg ratio on the microstructure and properties of Al-xZn-2.0Mg-1.0Cu-0.2Zr-yTi ultrahigh-strength aluminum alloy extrusion

Effect of Zn/Mg ratio on T6 state microstructure and properties of Al-xZn-2.6Mg-0.94Cu-0.2Zr-0.8Ti cold extruded aluminum alloy

Effect of Microstructure on Layered Double Hydroxides Film Growth on Mg-2Zn-xMn Alloy

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Effects of grain size and Al-Mn phase on the corrosion performance of hot-rolled AZ31 magnesium alloy

Microstructure and Corrosion Behavior of the As-cast Mg-xAl (x=9%, 12%, 15%) Alloys

Microstructure Characteristics and Corrosion Behaviors of Mg-2Zn-2Er-0.3Zr-0.3Mn Alloy under Various Rolling Reductions