Microstructure and tribological performance of Co-B intermetallic compounds under water environment

Yixuan He,Fan Bu,Yuhao Wu,Jiaqing Sun,Xibo Shao,Long Wang,Haifeng Wang

DOI: https://doi.org/10.1016/j.triboint.2023.109078

IF: 5.62

2023-11-05

Tribology International

Abstract:Cobalt-boride (Co-B) alloys, as promising wear resistant materials, can form different intermetallic compounds. In this work, supercooling treatment is applied to control the microstructures and compounds in the alloys, and the related mechanical and tribological properties have been investigated systematically. The results suggest that besides FCC-Co and HCP-Co, it forms Co 3 B and minor Co 2 B in the as-cast samples, Co 3 B, Co 2 B and Co 23 B 6 under different supercooling degree. Tribological experiments of these alloys under distilled water environment demonstrate that the Co-B alloy containing Co 23 B 6 has the best tribological performance, followed by Co 2 B and Co 3 B. The coefficient of friction and wear rate of alloy containing Co 23 B 6 are about 0.2 and 1.6×10 -6 mm 3 /Nm, respectively, which are reduced by 60% and one magnitude lower compared to the as-cast sample containing Co 2 B and Co 3 B. The promising tribological result of Co 23 B 6 is attributed to the formation of tribolayer, which is rich in Co(OH) 2 , silicate, SiO 2 and possibly H 3 BO 3 . This work provides guideline for tuning phases of Co-B alloys when using as rubbing parts in moisture environment.

engineering, mechanical