Abstract:Silicon carbide (SiC), as a representative of the third-generation semiconductor materials, is widely used in some fields which may suffer strong radiation such as in the cases of military affairs, aerospace and reactor. SiC possesses the superior radiation-resistance characteristic. However, SiC under the proton irradiation generate a lot of defects, resulting in degradation of device performance and even complete loss of its function. Therefore, the study on the irradiation damage to SiC under proton irradiation possesses important significance. A large number of studies have shown that for most of electronic devices and different types of incident particles, the degradation of device performance caused by displacement damage is linearly dependent on non-ionizing energy loss (NIEL), so the displacement damage can be evaluated by NIEL. In this work, the Monte Carlo software Geant4 is used to simulate the relationship between NIEL and proton energy, and the variation of NIEL with the depth of the material and the contribution of different types of primary recoil atoms to the total NIEL are also studied. The NIEL simulation results show that the NIEL in SiC material is less than that in Si and Ga semiconductor material under the same proton irradiation, proving that the stability and the radiation-resistance of SiC are stronger. The simulation results of NIEL at different depths show that the most serious damage regions of the material under different energy protons are diverse. Under the irradiation of low energy proton, the most serious region of the displacement damage occurs at the end of the proton range. With the increase of proton energy, the worst damage region of material will gradually move from the end of the proton range to the surface of SiC material. According to the contribution of different types of primary recoil atoms to the total NIEL, when the energy of the incident proton is low, the displacement damage of the proton in the SiC is mainly caused by 28Si and 12C, and the damage caused by 28Si is obviously higher than that by 12C. As the energy of proton increases, the 28Si and 12C are still the main causes of Bragg peak of the NIEL at the end of the proton range, but the number of ions generated by nuclear reactions increases accordingly, and the displacement damage caused by these ions increases in the shallow area of SiC, leading the surface of the material to be the worst damaged region. The combination of the two factors caused the most serious damage region moves from the end of the proton range to the surface of the material with the increase of proton energy. The results of this study are useful for the application of SiC devices to irradiation environment.

Response of commercial Si-IGBT to neutrons and direction dependency

Experimental study of pulse neutron irradiation damage in SiGe HBT

Atmospheric Neutron-induced Single Event Burnout Characterization of 4.5 kV Si IGBTs with Spallation Neutron Irradiation

Effects of neutron irradiation on SiGe HBT and Si BJT devices

Experimental and simulation studies of radiation‐induced single event burnout in SiC‐based power MOSFETs

Single-Event Effects in Heavy-Ion Irradiated 3kV SiC Charge-Balanced Power Devices

Comparison of Total Dose Effects on Sige Heterojunction Bipolar Transistors Induced by Different Swift Heavy Ion Irradiation

Irradiation effects of 25MeV silicon ions on SiGe heterojunction bipolar transistors

The reliability of SiGe HBT under swift heavy ion irradiation

Non-ionization Energy Loss of Proton in Different Regions in SiC

Impact of Heavy-Ion Irradiation on Gate Oxide Reliability of Silicon Carbide Power MOSFET

Transient synergistic damage mechanism and characterization of silicon bipolar junction transistor

Comparison of Neutron Irradiation Effects on the Electrical Performances of Sige Hbt and Si Bjt

Energy Dependence of Atmospheric Neutron-Induced Failures in Silicon Carbide Power Devices

Research of Single-Event Burnout in 1.2-kV Rated CoolSiC Trench MOSFET

Relating Gain Degradation to Defects Production in Neutron-Irradiated 4H-Sic Transistors

Degradation and Annealing Characteristics of NPN SiGe HBT Exposed to Heavy Ions Irradiation

Measurement and Analysis of Annealing Factor and Typical Dc Electronic Parameters for SiGe HBT Irradiated by Neutrons and Gamma Rays in a Pulsed Reactor

Total Ionizing Dose Effects of 60co Γ-Ray Radiation on Split-Gate SiC MOSFETs

Impact of Negative Gate Bias and Inductive Load on the Single-Pulse Avalanche Capability of 1200-V SiC Trench MOSFETs

The Degradation and Recovery of 1200-V SiC MOSFET with Different Total Ionizing Doses