Abstract:Elevated-temperature pressure swing adsorption is a promising technique for producing high purity hydrogen and controlling greenhouse gas emissions. Thermodynamic analysis indicated that the CO in H-2 rich gas could be controlled to trace levels of below 10 ppm by in situ reduction of the CO2 concentration to less than 100 ppm via the aforementioned process. The CO2 adsorption capacity of potassium-promoted hydrotalcite at elevated temperatures under different adsorption (mole fraction, working pressure) and desorption (flow rate, desorption time, steam effects) conditions was systematically investigated using a fixed bed reactor. It was found that the CO2 residual concentration before the breakthrough of CO2 mainly depended on the total amount of purge gas and the CO2 mole fraction in the inlet syngas. The residual CO2 concentration and uptake achieved for the inlet gas comprising CO2 (9.7 mL/min) and He (277.6 mL/min) at a working pressure of 3 MPa after 1 h of Ar purging at 300 mL/min were 12.3 ppm and 0.341 mmol/g, respectively. Steam purge could greatly improve the cyclic adsorption working capacity, but had no obvious benefit for the recovery of the residual CO2 concentration compared to purging with an inert gas. The residual CO2 concentration obtained with the adsorbent could be reduced to 3.2 ppm after 12 h of temperature swing at 450 degrees C. A new concept based on an adsorption/desorption process, comprising adsorption, steam rinse, depressurization, steam purge, pressurization, and high-temperature steam purge, was proposed for reducing the steam consumption during CO/CO2 purification. (C) 2017 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.

K‐Promoted Hydrotalcites for CO2 Capture in Sorption Enhanced Reactions

Ca based high temperature CO2 absorbents for sorption enhanced reforming process

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Elevated Pressure CO2 Adsorption Characteristics of K-promoted Hydrotalcites for Pre-combustion Carbon Capture

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Characteristics of MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure

Hydrothermal synthesis of K2CO3-promoted hydrotalcite from hydroxide-form precursors for novel high-temperature CO2 sorbent.

Study on CO2 Capture Performance by Potassium-Promoted MgAl-Hydrotalcite Adsorbent

Organic Anion Modified K-Promoted Hydrotalcite Adsorbent

Enhancement of CO2 Adsorption Performance on Hydrotalcites Impregnated with Alkali Metal Nitrate Salts and Carbonate Salts

Unexpected Highly Reversible Topotactic Co2 Sorption/Desorption Capacity For Potassium Dititanate

Self-Assembled Core-Shell Structure MgO@TiO2 as a K2CO3 Support with Superior Performance for Direct Air Capture CO2

The crucial role of the K+-aluminium oxide interaction in K+-promoted alumina- and hydrotalcite-based materials for CO2 sorption at high temperatures.

Experimental Characterization and Mechanistic Simulation of CO2 Adsorption/Desorption Processes for Potassium Promoted Hydrotalcites Sorbent

Design, characterization and scale-up test of a high performance pre-combustion CO2 adsorbent

Cost-effective carbon-based amine adsorbents for carbon capture: Equilibrium, kinetics and selectivity

High-Performance Co2 Adsorbent from Inter Layer Potassium-Promoted Stearate-Pillared Hydrotalcite Precursors

CO2 Residual Concentration of Potassium-Promoted Hydrotalcite for Deep CO/CO2 Purification in H2-rich Gas

Development of carboxyl-layered double hydrotalcites of enhanced CO 2 capture capacity by K 2 CO 3 promotion

Scalable synthesis of KNaTiO3-based high-temperature CO2 capture material from high titanium slag: CO2 uptake, kinetics, regenerability and mechanism study