Abstract:6-8 wt% yttria-stabilized zirconia (YSZ) has been widely employed as thermal barrier coating (TBC) to protect the high-temperature components of aero-engine and gas-turbine. However, the phase transition and sintering densification at high temperature seriously limit its application above 1200 °C. On account of this, CeO2 and Sc2O3 were doped into the YSZ by solid-state reaction sintering method in this paper. The effects of doping on the crystal structure, phase transition behavior and sintering resistance were investigated on the basis of XRD, Raman and FESEM, and the evolution of thermal properties of the ceramics was also analyzed. The results indicated that doped CeO2 increases the cell volume and tetragonal degree, but doped Sc2O3 was opposite. Co-doping caused not only significant difference in atomic mass and radius but also the formation of a large number of oxygen vacancies in the ceramics. Therefore, CeScYSZ showed the lowest thermal conductivity (1.53 W‧m−1‧K−1), which was about 23% lower than that of YSZ (2.00 W‧m−1‧K−1). More importantly, the oxygen vacancy also effectively stabilized the octet lattice, while the increase of lattice energy caused by Sc-O bond made it difficult for ions to misplace, which finally well prevented the transformation from t phase to m phase. There was no detrimental m-ZrO2 phase formation in the CeScYSZ after 120 h at 1500 °C. Besides, Co-doping could simultaneously overcome the poor sintering resistance caused by single CeO2 doping and the lower thermal expansion coefficient caused by single Sc2O3 doping, thus the CeScYSZ should be an ideal long-acting thermal protection material at higher temperatures.

Influence of various additions of Ti4+ substitution Ce4+ on high-temperature phase stability of co-precipitation Ti4+and Ce4+ co-doping YSZ powders

Effect of doping CeO2 and Sc2O3 on structure, thermal properties and sintering resistance of YSZ

Effect of TiO2 and Ta2O5 Co-Doping on Phase Stability, Fracture Toughness, and Sintering Behavior of ZrO2 Stabilized by 10Mol%(y0.4gd0.3yb0.3)2o3

Phase Composition and Stability, Sintering and Thermal Conductivity of Gd2O3 and Yb2O3 Co-Doped YSZ

Influence of Gd2O3 and Yb2O3 Co-doping on Phase Stability, Thermo-physical Properties and Sintering of 8YSZ

Phase evolution and hot corrosion behavior of Yb2O3 and CeO2 co-doping YSZ ceramics under high temperature

Improvement on the Phase Stability, Mechanical Properties and Thermal Insulation of Y2O3-stabilized ZrO2 by Gd2O3 and Yb2O3 Co-Doping

Preparation, Thermophysical Properties, and Thermal Shock Resistance of Yb2O3-doped YSZ Coatings

Role of a Low Level of La2O3 Dopant on the Tetragonal-to-monoclinic Phase Transformation of Ceria-Yttria Co-Stabilized Zirconia

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

Phase stability and thermal conductivity of ytterbia and yttria co-doped zirconia

Effect Of Ta2o5-Y2o3 Dopants On Phase Structure, Fracture Toughness And Thermophysical Properties Of Zirconia

Effect of CeO2 doping on high temperature oxidation resistance of YSZ TBCs

Effect of modulating the phase structure of YSZ ceramics by TiO 2 doping on the CMAS corrosion resistance at 1250 °C

Effects of co-precipitation temperature on structure and properties of La and Y doped cerium zirconium mixed oxides

Influence of Partial Substitution of Sc2o3 with Gd2o3 on the Phase Stability and Thermal Conductivity of Sc2o3-Doped Zro2

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Determinations of Ce Solid Solution Mechanism and Limit Thermal Conductivity of YTaO4 Ceramics

Effect of Yttrium Doping on Oxygen Storage Capacity of Ce_(0.33)Zr_(0.67)O_2

Effect of lattice defects on thermal conductivity of Ti-doped, Y 2O3-stabilized ZrO2

Phase Stability, Thermophysical Properties, Thermal Cycling, and CMAS Resistance of 16ce4ybsz Coating