Effect of modulating the phase structure of YSZ ceramics by TiO 2 doping on the CMAS corrosion resistance at 1250 °C

Xiaodong Wei,Zhicheng Zhao,Yulong An,Huidi Zhou,Jianmin Chen

DOI: https://doi.org/10.1016/j.ceramint.2023.01.053

IF: 5.532

2023-03-29

Ceramics International

Abstract:YSZ and TiO 2 doped YSZ (TYSZ) sintered compacts were prepared in this study, and the modulation behaviors of Ti 4+ doping on the microstructure and phase structure of YSZ ceramics were comparatively investigated, while the optimization mechanisms of Ti 4+ doping on the CMAS corrosion resistance of YSZ ceramics were elucidated from these two aspects. The results indicate that although the small grain size and high densification of YSZ can mitigate CMAS infiltration at the early stage of corrosion, the high contact specific surface area of YSZ with CMAS caused by such small grains is the main reason for the rapid degradation of the samples at the later stage of corrosion. TYSZ has a higher c-phase content than YSZ, and the presence of a large amount of structurally stable c-phase was one of the main reasons for the outstanding resistance to CMAS corrosion of TYSZ. In addition, the segregation of Y and Ti elements into the surrounding CMAS was responsible for the t-m phase transition. The generated m-phase both provided a channel to segregate elements inside the grains and was easily dissolved in the CMAS, which eventually completely degraded ZrO 2 -based ceramics in CMAS.

materials science, ceramics