Abstract:Porous MgO based ceramics have been widely used in some key industries due to their excellent performance. To investigate the feasibility of preparing porous magnesia ceramics using magnesite tailings as a magnesium source. Porous MgO based ceramics were prepared using magnesite tailings, fused magnesia as main raw materials and soluble starch as pore-forming agent. The starting materials were mixed in different ratios and sintered at 1500 °C for 2 h to obtain good mechanical and thermophysical properties. The Mg 2 SiO 4 plays a fixing role, inhibiting the growth of MgO grains and further promoting the discharge of pores. This fixation can prevent the linear expansion of cracks, thus increasing the fracture surface energy of the specimen. In addition, the scattering effect of pores on gas molecules decreases as the magnesite tailings content increase, so that the thermal conductivity increases. The results showed that when the mass ratio of magnesite tailings to fused magnesia was increased from 1:1 to 1:0 with 4 wt% soluble starch as the pore-forming agent, the apparent porosity decreased from 35.59% to 11.8%; the bulk density increased from 2.37 to 2.82 g∙cm −3 ; the linear shrinkage ratio increased from 9.28 to 24.23%; the cold compressive strength increased from 47.75 to 226.52 MPa; the residual strength retention rate after one thermal shock cycles at 1100 °C was between 64.05 and 87.76%; and the thermal conductivity increased from 7.44 to 12.23 W∙m −1 K −1 .

Porosity properties of porous ceramic substrates added with zinc and magnesium material

Porosity effect on the functional properties and energy harvesting performance of Ba0.85Ca0.15Ti0.90Zr0.10O3 ceramics

Microstructure and mechanical properties of a porous ceramic composite with needle‐like mullite and zirconia

Ceramic Material Porous Structure Prepared Using Pore-Forming Additives

Preparation and Properties of Porous ZTM Ceramics

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia

Effects of porosity and pore size on mechanical and thermal properties as well as thermal shock fracture resistance of porous ZrB2–SiC ceramics

Effect of adding ways of calcium zirconate on performance of MgO-CaZrO3 based dispersed porous refrac-to ry

Preparation and Characterization of YSZ Porous Ceramic Tubes with a High Porosity by Wet Method

Effect of the different additives on the fabrication of porous kaolin-based mullite ceramics

Preparation of Porous Spodumene/zircon Composite Ceramics and Its Thermal and Mechanical Properties

Preparation and properties of porous ceramics based on alumomagnesium spinel and zirconium dioxide

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Preparation and Characterization of Tubular Porous Ceramics from Natural Zeolite

Effect of Porosity on Functional Properties of Lead-Free Piezoelectric BaZr0.15Ti0.85O3 Porous Ceramics

Low sintering shrinkage and high strength of porous mullite–zirconia ceramics: Effect of AlF3 and ZrSi2 contents

Porosity and Electrical Properties of Porous PZT 95/5 Ferroelectric Ceramics

Multiple layers, porous surface, and their role in increasing the efficiency of photocatalytic coating on (DD3, DD3+ZrO 2 ) ceramics and glass

Cu:ZnO deposited on porous ceramic substrates by a simple thermal method for photocatalytic application

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Properties of porous magnesia‐stabilized zirconia ceramics fabricated by slurry infiltration into polyurethane foam