Abstract:Porous MgO based ceramics have been widely used in some key industries due to their excellent performance. To investigate the feasibility of preparing porous magnesia ceramics using magnesite tailings as a magnesium source. Porous MgO based ceramics were prepared using magnesite tailings, fused magnesia as main raw materials and soluble starch as pore-forming agent. The starting materials were mixed in different ratios and sintered at 1500 °C for 2 h to obtain good mechanical and thermophysical properties. The Mg 2 SiO 4 plays a fixing role, inhibiting the growth of MgO grains and further promoting the discharge of pores. This fixation can prevent the linear expansion of cracks, thus increasing the fracture surface energy of the specimen. In addition, the scattering effect of pores on gas molecules decreases as the magnesite tailings content increase, so that the thermal conductivity increases. The results showed that when the mass ratio of magnesite tailings to fused magnesia was increased from 1:1 to 1:0 with 4 wt% soluble starch as the pore-forming agent, the apparent porosity decreased from 35.59% to 11.8%; the bulk density increased from 2.37 to 2.82 g∙cm −3 ; the linear shrinkage ratio increased from 9.28 to 24.23%; the cold compressive strength increased from 47.75 to 226.52 MPa; the residual strength retention rate after one thermal shock cycles at 1100 °C was between 64.05 and 87.76%; and the thermal conductivity increased from 7.44 to 12.23 W∙m −1 K −1 .

Properties of porous magnesia‐stabilized zirconia ceramics fabricated by slurry infiltration into polyurethane foam

Porous yttria-stabilized zirconia ceramics with low thermal conductivity via a novel foam-gelcasting method

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Processing and properties of porous PZT ceramics from particle-stabilized foams via gel casting

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting

Fabrication of Ceramics with Complex Porous Structures by the Impregnate–Freeze‐Casting Process

A Novel Method Based on Ultrastable Foam and Improved Gelcasting for Fabricating Porous Mullite Ceramics with Thermal Insulation–mechanical Property Trade-off

Characterization of Magnesia Foam Ceramics Prepared by Foam Impregnation and Its Application in Crude Magnesium Refining

Design and Formulation of Polyurethane Foam Used for Porous Alumina Ceramics

Highly Porous Zirconia Ceramic Foams with Low Thermal Conductivity from Particle‐Stabilized Foams

Foam-gelcasting preparation and properties of high-strength mullite porous ceramics

Fabrication of Porous Ceramics by Direct Foaming

Effects of Foam Composition on the Microstructure and Piezoelectric Properties of Macroporous PZT Ceramics from Ultrastable Particle-Stabilized Foams

Performance magnesia porous insulation materials preparation process research

Fabrication of Porous Zirconia Ceramics by Injection Molding Method

Structure and properties study of magnesium oxide porous ceramics prepared by Organic Foam Template Method

Preparation and Mechanical Properties of Light-Weight Porous Magnesium Stabilized Zirconia Refractories

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia

Highly Porous and Hierarchical MgAl2O4 Ceramics with Improved Pore Connectivity Prepared from Gelled Particle-Stabilized Foams

A novel highly porous ceramic foam with efficient thermal insulation and high temperature resistance properties fabricated by gel-casting process

Fabrication of porous PZT ceramics using micro-stereolithography technology