Abstract:In this study, two kinds of MgO ceramic filters were prepared by using porous magnesia powder and fused magnesia powder as raw material, respectively. The microstructures, mechanical properties and purification efficiency on the molten steel of two MgO ceramic filters were investigated by mercury porosimetry measurement, SEM, EDS and immersion test with molten steel, etc. The results demonstrate that compared with the filter FM prepared from the fused magnesia powder, the rheological property of the slurry of the filter PM was improved via the finer and uniformly distributed nano-sized Mg(OH) 2 particles generated by the hydration of the porous magnesia powder, which not only optimized the macropore structure but also promoted the growth of the sintering neck between the microparticles of the skeleton. Therefore, the MgO filter skeleton with a microporous structure was obtained, which elevated the strength and thermal shock resistance of the filter PM. According to the immersion tests with the molten steel, both filters significantly reduced the number of inclusions with size < 5 μm 2 in the molten steel as well as their total oxygen contents, and the filter PM had better purification efficiency than the filter FM. The reason for the better purification efficiency of the filter PM was related to its smaller micro-sized pores, larger surface roughness, and certain high-temperature liquid phase in their skeletons. In general, the porous magnesia powder resulted in higher compressive strength, better thermal shock resistance and superior purification efficiency on the molten steel of the filter compared with the fused magnesia powder.

Characterization of Magnesia Foam Ceramics Prepared by Foam Impregnation and Its Application in Crude Magnesium Refining

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Factors affecting the microstructure of a fine ceramic foam

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia

Properties of porous magnesia‐stabilized zirconia ceramics fabricated by slurry infiltration into polyurethane foam

Structure and properties study of magnesium oxide porous ceramics prepared by Organic Foam Template Method

Foam-gelcasting preparation and properties of high-strength mullite porous ceramics

Effects of magnesite addition on the properties and structure of foam ceramics

Preparation and characterization of SiO2–Al2O3–MgO–CaO–based ceramic foams mainly from Ca–Mg–rich molybdenum tailings

One-pot Synthesis of Foam-Like Magnesia and Its Performance in CO2 Adsorption

Performance magnesia porous insulation materials preparation process research

Highly Porous and Hierarchical MgAl2O4 Ceramics with Improved Pore Connectivity Prepared from Gelled Particle-Stabilized Foams

Preparation of high performance MgO ceramic filter and its interaction with molten steel: Effect of porous MgO powder

Magnesium Metal Foam Production Using Polypropylene Fibers as an Active Hydrogen Source

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Effects of Foaming Agent on Microstructure and Properties of Porous Mullite Ceramics

A Novel Method Based on Ultrastable Foam and Improved Gelcasting for Fabricating Porous Mullite Ceramics with Thermal Insulation–mechanical Property Trade-off

Pure Mg foams stabilized by CaO particles

Effect of Blowing-Agent Addition on the Structure and Properties of Magnesia Porous Material

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting

Fabrication of Clay Foam Ceramics Using Silicon Carbide and Ferric Oxide as Foaming Agents