Abstract:Porous MgO based ceramics have been widely used in some key industries due to their excellent performance. To investigate the feasibility of preparing porous magnesia ceramics using magnesite tailings as a magnesium source. Porous MgO based ceramics were prepared using magnesite tailings, fused magnesia as main raw materials and soluble starch as pore-forming agent. The starting materials were mixed in different ratios and sintered at 1500 °C for 2 h to obtain good mechanical and thermophysical properties. The Mg 2 SiO 4 plays a fixing role, inhibiting the growth of MgO grains and further promoting the discharge of pores. This fixation can prevent the linear expansion of cracks, thus increasing the fracture surface energy of the specimen. In addition, the scattering effect of pores on gas molecules decreases as the magnesite tailings content increase, so that the thermal conductivity increases. The results showed that when the mass ratio of magnesite tailings to fused magnesia was increased from 1:1 to 1:0 with 4 wt% soluble starch as the pore-forming agent, the apparent porosity decreased from 35.59% to 11.8%; the bulk density increased from 2.37 to 2.82 g∙cm −3 ; the linear shrinkage ratio increased from 9.28 to 24.23%; the cold compressive strength increased from 47.75 to 226.52 MPa; the residual strength retention rate after one thermal shock cycles at 1100 °C was between 64.05 and 87.76%; and the thermal conductivity increased from 7.44 to 12.23 W∙m −1 K −1 .

Structure and properties study of magnesium oxide porous ceramics prepared by Organic Foam Template Method

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Factors affecting the microstructure of a fine ceramic foam

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia

Foam-gelcasting preparation and properties of high-strength mullite porous ceramics

Recent Progress in Porous Mg-based Foam Preparation Approaches: Effect of Processing Parameters on Structure and Mechanical Property

Performance magnesia porous insulation materials preparation process research

Highly Porous and Hierarchical MgAl2O4 Ceramics with Improved Pore Connectivity Prepared from Gelled Particle-Stabilized Foams

Effects of Foaming Agent on Microstructure and Properties of Porous Mullite Ceramics

In-situ synthesis and properties of porous cordierite ceramics with adjustable pore structure

Effects of Ammonium Molybdate Additive and Sintering Temperature on the Properties of Foam Ceramics Based on Ceramic Tile Polishing Waste

Porous MgO-based ceramics synthesized by the volume expansion effect: Designing and performance

Preparation of Porous Ceramic Materials by Alumina Fiber Framework

Formation of closed pore structure in CaO-MgO-Al2O3-SiO2 (CMAS) porous glass-ceramics via Fe2O3 modified foaming for thermal insulation

Low-Temperature Reactive Sintered Porous Mg-Al-Zn Alloy Foams

Preparation of foam ceramics from solid wastes: a study on the relationship between firing regime and properties by grey system theory

Effect of Blowing-Agent Addition on the Structure and Properties of Magnesia Porous Material

Effects of magnesite addition on the properties and structure of foam ceramics

Effects of sintering temperature on properties of porous mullite/corundum ceramics

Characterization of Magnesia Foam Ceramics Prepared by Foam Impregnation and Its Application in Crude Magnesium Refining

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting