New insight into magneto-structural phase transitions in layered TbMn2Ge2-based compounds
Chunsheng Fang,Guoxing Li,Jianli Wang,W. D. Hutchison,Q. Y. Ren,Zhenyan Deng,Guohong Ma,Shixue Dou,S. J. Campbell,Zhenxiang Cheng
DOI: https://doi.org/10.1038/srep45814
IF: 4.6
2017-04-01
Scientific Reports
Abstract:The Tb1−xYxMn2Ge2 series (x = 0, 0.1, 0.2) compounds are found to exhibit two magnetic phase transitions with decreasing temperature: from the paramagnetic state to the antiferromagnetic interlayer state at TNinter and from an antiferromagnetic interlayer structure to a collinear ferrimagnetic interlayer structure at TCinter. Compared with the slight change of TNinter (409 K, 410 K and 417 K for x = 0, 0.1 and 0.2 respectively), the replacement of Y for Tb leads to a significant decrease in TCinter from 97.5 K for x = 0 to 74.6 K for x = 0.2. The variation in TCinter can be ascribed to the combination of two effects: (1) chemical pressure and (2) magnetic dilution effect by Y substitution for Tb. Besides, a strong anisotropic magnet-volume effect has been detected around TCinter in all compounds with Δa/a = 0.125%, 0.124% and 0.130% for x = 0, 0.1 and 0.2, respectively while no obvious effect is detected along the c-axis. The maximum magnetic entropy change were found to be −ΔSmax = 9.1 J kg−1 K−1, 11.9 J kg−1 K−1 and 6.3 J kg−1 K−1 with a field change from 0 T to 5 T for x = 0, 0.1, 0.2 respectively.
multidisciplinary sciences