Study on the Structure Magnetostriction and Spin Reorientation of Tb_(0.3)Dy_(0.7)(Fe_(1-x)Al_x)_(1.95) Alloys

Zheng Xiaoping

2003-01-01

Abstract:The effect of Al substitution for Fe on the structure,magnetostriction,anisotropy and spin reorientation of a series of Tb_ 0.3 Dy_ 0.7 (Fe_ 1-x Al_x)_ 1.95 alloys(x=0,0.05,0.1,0.15,0.20,0.25,0.30,0.35) at room temperature has been investigated.It was found that all compositions of Tb_ 0.3 Dy_ 0.7 (Fe_ 1-x Al_x)_ 1.95 substantially retained the MgCu_2-type C-15 cubic Laves phase structure and the lattice constant increases with increasing x.The substitution of Al increases slightly the magnetostriction in a low magnetic field (H ≤40kA/m) when x0.15,while the magnetostriction decreases sharply,but is saturated more easily with increasing x in a higher applied field and the magnetostrictive effect disappears at x0.15.The intrinsic magnetostriction λ_ 111 decreases sharply also with incresasing x.The Mssbauer spectra show that the easy magnetization direction(EMD) of Tb_ 0.3 Dy_ 0.7 (Fe_ 1-x Al_x)_ 1.95 may deviate slightly from the major axis of symmetry 111 with the component and temperature,i.e.spin reocientation are present.A small amount of non-magnetic phase exists for x=0.15 and the alloys become paramagnetism when x0.15.