A Study of the Magnetism, Magnetostriction and M(o)ssbauer of Tb0.3Dy0.7(Fe1-xAIx)1.95 Alloys

ZHENG Xiao-ping,ZHANG Pei-feng,LI Fa-shen,CHENG Zhao-hua,SHEN Bao-gen

DOI: https://doi.org/10.3321/j.issn:0455-2059.2007.03.021

2007-01-01

Abstract:The effect of Al substitution for Fe on the magnetic and magnetostrictive properties, the spin reorientation and Mossbauer spectra of a series of Tb0.3Dy0.7(Fe1-xAlx)1.95 alloys (x=0, 0.05, 0.1, 0.15, 0.20, 0.25, 0.30, 0.35) at room temperature and 77 K has been systemically investigated. It was found that the primary phase of Tb0.3Dy0.7(Fe1-xAlx)1.95 is the MgCu2-type cubic laves phase structure when x 0.4. The magnetization and magnetostriction measurements showed that a small amount of Al substitution is beneficial to a decrease in the magneto crystalline anisotropy for x 0.15, and that the magnetostriction, the spontaneous magnetostrictionλ111 and the Curie temperature Tc decrease greatly. The study of PPMS and Mossbauer indicated that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the changes of composition and temperature, namely spin reorientation. A small amount of non-magnetic phase exists for x = 0.15 in Tb0.3Dy0.7(Fe1-xAlx)1.95 alloys and the alloys become paramagnetic for x 0.15 at room temperture, but at 77 K the alloys still remain in magnetic phase even for x = 0.2.