A Study of Magnetostriction, Spin Reorientation, and Mössbauer Spectra of Tb 0.3 Dy 0.6 Pr 0.1 (fe 1− X Al X ) 1.95 Alloys with Substitution of Fe by Al

XiaoPing Zheng,PeiFeng Zhang,FaShen Li,Yuan Hao

DOI: https://doi.org/10.1007/s11433-010-0089-y

2010-01-01

Abstract:The effects of Al substitution for Fe on the structure, magnetics, magnetostriction, anisotropy and spin reorientation of a series of Tb0.3Dy0.6Pr0.1(Fe1−x Al x )1.95 alloys (x=0.05, 0.1, 0.15, 0.2, 0.25, 0.3) at room temperature have been investigated. The alloys of Tb0.3Dy0.6Pr0.1(Fe1−x Al x )1.95 substantially retain MgCu2-type C-15 cubic Laves phase structure when x<0.2. The mixed phases appear with x = 0.2, and cubic Laves phase decreases with increasing x. The magnetostriction of the Tb0.3Dy0.6Pr0.1(Fe1−x Al x )1.95 alloys decreases drastically with increasing x and the giant magnetostrictive effect disappears for x > 0.15. Fortunately, a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. The spin reorientation temperature decreases with increasing x. The analysis of the Mössbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the increase of Al concentration x, namely, spin reorientation, resulting in the change of macroscopical magnetic properties and magnetostriction. The hyperfine field decreases, but the isomer shifts increases with Al concentration increasing and the quadruple splitting QS shows a weak concentration dependence.