Nonhysteretic metamagnetic phase transition in Ho2In1-xAlx (0 ≤ x ≤ 0.4) by hetero-structural alloying

Rui Liu,Shengyu Sun,Guiquan Yao,Qiang Wang,Peng Tong,Jie Zhu,Sen Yang,Weibin Cui

DOI: https://doi.org/10.1016/j.jmmm.2021.168305

IF: 3.097

2021-11-01

Journal of Magnetism and Magnetic Materials

Abstract:By hetero-structural alloying ferromagnetic hexagonal Ho2In with antiferromagnetic orthorhombic Ho2Al, the magnetic and structural changes have been observed in Ho2In1- x Al x (0 ≤ x ≤ 0.4) alloys. At the critical composition x = 0.1, the highest maxima of magnetic entropy change of 16.3 Jkg-1K−1 and the adiabatic temperature change of 6.5 K have been obtained via an unconventional hysteresis-free metamagnetic phase transitionm, which is higher than 9 Jkg-1K−1 and 5.4 K in Ho2In benchmark alloy undergoing second-order phase transition. Such increment is associated with the intensified magnetoelastic coupling. The deeper origin is proposed to be from the delocalized 5d electrons of rare-earth atoms by external field since the magnetoresistence is also maximized at the critical composition. The hetero-structural alloying strategy is demonstrated to be effective to intensify the MCE effect without causing the undesirable hysteresis.

materials science, multidisciplinary,physics, condensed matter

What problem does this paper attempt to address?

The paper primarily explores the issue of achieving non-hysteretic magneto-structural phase transitions in the Ho2In1-xAlx (0 ≤ x ≤ 0.4) system through a heterogeneous alloying method, thereby enhancing the magnetocaloric effect (MCE).

Specifically, the researchers observed the magnetic and structural changes in the Ho2In1-xAlx (0 ≤ x ≤ 0.3) alloys by heterogeneously alloying the ferromagnetic hexagonal structure Ho2In with the antiferromagnetic orthorhombic structure Ho2Al. Notably, at the critical composition of x = 0.1, the highest magnetic entropy change value of 16.3 J/kg·K and adiabatic temperature change value of 6.5 K were achieved through an unconventional non-hysteretic magneto-structural phase transition. These values are significantly higher than the 9 J/kg·K and 5.4 K of the pure Ho2In alloy. This enhancement is believed to be related to the intensification of magnetoelastic coupling, and the underlying reason may be the delocalization of 5d electrons of rare earth atoms under the influence of an external magnetic field.

In summary, this paper aims to enhance the magnetocaloric effect in magnetic refrigeration materials through a specific alloying strategy while avoiding the unfavorable hysteresis phenomenon that usually accompanies first-order phase transitions.