Abstract:The preparation of β-hemihydrate gypsum is an important approach for large-scale utilization of phosphogypsum (PG) because of the simple production technology by calcination. However, the dehydration behaviour and impurity change during the transformation of PG to β-hemihydrate gypsum at low temperatures are unclear. In this study, the dehydration of PG at different temperatures was investigated by a calcination test and in-situ X-ray diffraction analysis. The variation in crystal morphology and structure of PG was clarified using scanning electron microscopy and Materials Studio software. Furthermore, the change of impurity was analyzed by energy-dispersive spectroscopy, Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy measurements. The results show that the dehydration of PG to β-hemihydrate gypsum depends on calcination temperature and time. Moreover, an increase in the calcination temperature could accelerate the dehydration of PG and shorten the dehydration time; meanwhile increasing the calcination time or calcination temperature could make a part of β-hemihydrate gypsum further dehydrate to anhydrite. The morphology and elemental distribution of PG did not dramatically change during calcination, but the grain size decreased and the elemental distribution density increased. It should be noted that the calcination did not decrease the phosphorus and fluorine contents in PG at 120 °C, whereas the contents increased due to the removal of crystal water. The phosphorus impurity form transformed from CaHPO4·2H2O and Ca(H2PO4)2·H2O to CaHPO4 and Ca(H2PO4)2, respectively. Therefore, the calcination could not remove the phosphorus and fluorine from PG, and pretreatment is required to reduce the adverse effects of impurities in the industrial production of β-hemihydrate gypsum.

Dehydration behaviour and impurity change of phosphogypsum during calcination

Efficient precipitation of soluble phosphorus impurities in the recycling of phosphogypsum to produce hemihydrate gypsum

Preparation of Anhydrite from Phosphogypsum: Influence of Phosphorus and Fluorine Impurities on the Performances

Effect of Fluorine and Phosphorus Impurities in Phosphogypsum on Microstructure and Mechanism of α‐Type Hemihydrate Gypsum Crystals

The study on the effect of flotation purification on the performance of α-hemihydrate gypsum prepared from phosphogypsum

Study on Mechanisms for Improving Quality and Whiteness of Phosphogypsum Based on Process Mineralogy Analysis

Efficient removal of impurities from phosphogypsum during preparation of α-hemihydrate gypsum

Influence of calcination and GGBS addition in preparing β-hemihydrate synthetic gypsum from phosphogypsum

Efficient extraction of impurities from phosphogypsum during crystal regulation of α‐hemihydrate gypsum

Hydration reaction and microstructural characteristics of hemihydrate phosphogypsum with variable pH

Gradient removal of Si and P impurities from phosphogypsum and preparation of anhydrous calcium sulfate

Mechanism of calcination modification of phosphogypsum and its effect on the hydration properties of phosphogypsum-based supersulfated cement

Study on the occurrence state of main components of phosphogypsum dihydrate and its impurity distribution

Simultaneous removal of phosphorus and organic contaminants from phosphogypsum using hydrothermal method for gypsum resource regeneration

Dehydration Behavior of FGD Gypsum by Simultaneous TG and DSC Analysis

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions

Effect of calcination temperature and superplasticizer on the properties of anhydrite II from phosphogypsum

Retarding effect of impurities on the transformation kinetics of FGD gypsum to α-calcium sulfate hemihydrate under atmospheric and hydrothermal conditions

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Effect of soluble fluorine on the hydration, strength and microstructure of hemihydrate phosphogypsum

Effect of Ph on the Preparation of Alpha-Calcium Sulfate Hemihydrate from Fgd Gypsum with the Hydrothermal Method