Abstract:The preparation of β-hemihydrate gypsum is an important approach for large-scale utilization of phosphogypsum (PG) because of the simple production technology by calcination. However, the dehydration behaviour and impurity change during the transformation of PG to β-hemihydrate gypsum at low temperatures are unclear. In this study, the dehydration of PG at different temperatures was investigated by a calcination test and in-situ X-ray diffraction analysis. The variation in crystal morphology and structure of PG was clarified using scanning electron microscopy and Materials Studio software. Furthermore, the change of impurity was analyzed by energy-dispersive spectroscopy, Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy measurements. The results show that the dehydration of PG to β-hemihydrate gypsum depends on calcination temperature and time. Moreover, an increase in the calcination temperature could accelerate the dehydration of PG and shorten the dehydration time; meanwhile increasing the calcination time or calcination temperature could make a part of β-hemihydrate gypsum further dehydrate to anhydrite. The morphology and elemental distribution of PG did not dramatically change during calcination, but the grain size decreased and the elemental distribution density increased. It should be noted that the calcination did not decrease the phosphorus and fluorine contents in PG at 120 °C, whereas the contents increased due to the removal of crystal water. The phosphorus impurity form transformed from CaHPO4·2H2O and Ca(H2PO4)2·H2O to CaHPO4 and Ca(H2PO4)2, respectively. Therefore, the calcination could not remove the phosphorus and fluorine from PG, and pretreatment is required to reduce the adverse effects of impurities in the industrial production of β-hemihydrate gypsum.

Hydration reaction and microstructural characteristics of hemihydrate phosphogypsum with variable pH

Influence mechanism of alkaline environment on the hydration of hemihydrate phosphogypsum: A comparative study of various alkali

Study on physical and chemical characteristics of β-hemihydrate phosphogypsum

Enhancing the hydration reactivity of hemi-hydrate phosphogypsum through a morphology-controlled preparation technology

Investigation on the hydration of hemihydrate phosphogypsum after post treatment

Effect of neutralization on the setting and hardening characters of hemihydrate phosphogypsum plaster

Efficient precipitation of soluble phosphorus impurities in the recycling of phosphogypsum to produce hemihydrate gypsum

Improving mechanical properties of hemihydrate phosphogypsum via alkali-activated mineral admixtures

The Influences of Soluble Phosphorus on Hydration Process and Mechanical Properties of Hemihydrate Gypsum under Deep Retarding Condition

Effect of Soluble Phosphorus on the Mechanical Properties of α-Hemihydrate Gypsum

Effect of Soluble P2O5 Form on the Hydration and Hardening of Hemihydrate Phosphogypsum

Recycling of waste gypsum from αlpha-hemihydrate phosphogypsum: Based on the atmospheric hydrothermal process

Hydration Mechanism and Hardening Property of α-Hemihydrate Phosphogypsum

Dehydration behaviour and impurity change of phosphogypsum during calcination

Study on the Kinetics of Hydration Transformation from Hemihydrate Phosphogypsum to Dihydrate Phosphogypsum in Simulated Wet Process Phosphoric Acid

Activation of anhydrate phosphogypsum by K2SO4 and hemihydrate gypsum

Effect of Fluorine and Phosphorus Impurities in Phosphogypsum on Microstructure and Mechanism of α‐Type Hemihydrate Gypsum Crystals