Wet-process phosphoric acid for preparation of iron phosphate and its influence on performance of lithium iron phosphate synthesis

Ding Yi-gan

Abstract:Iron phosphate was prepared using wet-process phosphoric acid as phosphorus source and ferrous sulfate as iron source through the synthesis and precipitation process. The influence of different molar weight ratio on the quality of synthetic iron phosphate was studied,and lithium iron phosphate anode material prepared using iron phosphate as the phosphorus source and iron source through the method of sor- gel. Structure and microstructure of the lithium iron phosphate material were characterized by X- ray diffraction and scanning electron microscope,and its electrochemical properties also were investigated. The results show that the phosphorus content of the prepared iron phosphate is 16.38% and iron content is 29.30% when the molar ratio of wet-process phosphoric acid and ferrous sulfate is 1∶1,the product closing to two water's iron phosphate. The lithium iron phosphate anode material prepared using the iron phosphate was chargeddischarged under 0.1C ratio,its first specific discharge capacity reaching up to 144.4 mAh/g. Finally the discharge capacity reaches to 141.6 mAh/g. and the attenuation rate is 1.94% after 40 times charge-discharge cycle,which demonstrates a excellent performance circulating rate.

Chemistry,Materials Science