On factors defining the mechanical behavior of nanoporous gold
Birthe Zandersons,Lukas Lührs,Yong Li,Jörg Weissmüller
DOI: https://doi.org/10.1016/j.actamat.2021.116979
IF: 9.4
2021-08-01
Acta Materialia
Abstract:<p>Nanoporous gold (NPG) made by dealloying takes the form of a network of nanoscale struts or "ligaments". It is well established that the material's mechanical behavior is strongly affected by its ligament size, <span class="math"><math>L</math></span>, and by its solid volume fraction, <span class="math"><math>φ</math></span>. We explore the mechanical behavior of NPG, with an emphasis on establishing a consistent data set with comparable <span class="math"><math>L</math></span> but covering a significant range of initial <span class="math"><math>φ</math></span>. Specimens are prepared from Ag-Au master alloys with their Au atom fraction, <span class="math"><math>xAu0</math></span>, in the range 0.20 - 0.35. Since dealloying replaces Ag with voids, <span class="math"><math>φ</math></span> may be expected to agree with <span class="math"><math>xAu0</math></span>. Yet, spontaneous plastic deformation events during dealloying can result in macroscopic shrinkage, decoupling <span class="math"><math>φ</math></span> from <span class="math"><math>xAu0</math></span>. This raises the question, how do <span class="math"><math>φ</math></span> and <span class="math"><math>xAu0</math></span> separately affect the mechanical behavior? We confirm two recent suggestions, namely i) a modified Roberts-Garboczi-type scaling law for Young's modulus versus <span class="math"><math>φ</math></span> of the material in its as-prepared state and ii) the relevance of an apparent "load-bearing solid fraction" for Young's modulus as well as strength. Yet, remarkably, we find that stiffness and strength of the as-prepared material show a much better correlation to <span class="math"><math>xAu0</math></span> as compared to <span class="math"><math>φ</math></span>. This can be understood as a consequence of the microstructural changes induced by shrinkage. Studying the microstructure evolution during annealing, we also confirm the suggestion that coarsening entails an enhanced loss in stiffness for samples with lesser solid fraction. This finding confirms concerns about the notion of self-similar coarsening as a general behavior of dealloying-made network materials.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering