Abstract:In contrast to austenitic and martensitic stainless steels, ferritic stainless steels have a lower hardness and wear resistance but exhibit excellent corrosion resistance. Due to this fact, their use in the aerospace, automobile, and house construction industries is restricted. Several methods have been utilized to enhance the tribological characteristics of ferritic stainless steels. In this work, titanium nitride coating has been carried out by using a cathodic cage of titanium material, and later on, the titanium cathodic cage is replaced by an AISI-304 cathodic cage in a CCPN chamber to form iron nitride coating on AISI-430 ferritic stainless steel coupons through a plasma nitriding process for 4 h at a fixed temperature of 400 °C. The microstructures and mechanical traits of all processed and control coupons were analyzed using scanning electron microscopy, X-ray diffraction, ball-on-disc wear tester, and microhardness tester techniques. The results showed that hardness increased up to 1489 HV with the titanium cage, which is much higher than the hardness of the base material (270 HV). The titanium cage-treated coupons have high layer thickness, smooth surface morphology, and a minimum crystallite size of 2.2 nm. The wear rate was reduced up to 50% over the base material after the titanium cage plasma treatment. The base coupon exhibited severe abrasive wear, whereas nitrided coupons exhibited dominant adhesive wear. In the iron nitride coatings, this effect is also important, owing to the more influential cleaning process in a glow discharge, and the better adhesion with enhanced interlayer thickness is attributed to the fact that the compliance of the interlayer minimizes shear stresses at the coating-substrate interface. The use of a graded interface improves adhesion compared with the case where no interlayer is used but a titanium interlayer of comparable thickness provides a significant increase in measured adhesion. For both titanium and iron nitride films, there is a reduction in wear volume which is a function of interlayer thickness; this will have a substantial effect on wear lifetime. Thus by careful control of the interlayer thickness and composition, it should be possible to improve coating performance in tribological applications.

Study of the Properties of Iron and Vanadium Nitride Coatings by CCPD on 1080 Steel

Two-Layer Nanocomposite TiC-Based Coatings Produced by a Combination of Pulsed Cathodic Arc Evaporation and Vacuum Electro-Spark Alloying

Surface Analysis of AISI D2 Steel Treated by Plasma Nitriding and Niobium and Vanadium Nitride Films by Cathodic Cage Plasma Deposition

Surface modification of AISI-420 steel by cathodic cage plasma niobium nitride deposition

Study on mechanical properties and corrosion resistance of VC nanoparticles reinforced Ni-W coatings

Improved Adhesion and Tribological Properties of AlTiN-TiSiN Coatings Deposited by DCMS and HiPIMS on Nitrided Tool Steels

Improved wear resistance of AISI-4340 steel by Ti–Nb–C–N and MoS 2 composite coating by cathodic cage plasma deposition

Optimization of Black Nickel Coatings’ Electrodeposit onto Steel

Study on Microstructure and Properties of FeNiCr/Ni Coated Cr_3C_2 Coatings Deposited by High Velocity Arc Spraying

Study of the Role of Titanium and Iron Cathodic Cages on Plasma-Nitrided AISI 430 Ferritic Stainless Steel

Nanoindentation and Tribological Behavior of TiN-TiCN-TiAlN Multilayer Coatings on AISI D3 Tool Steel

On the Effect of Aluminum on the Microstructure and Mechanical Properties of CrN Coatings deposited by HiPIMS

Graded and Single-Layer NiAl/WC-Co Coatings Processed by Plasma Transferred Arc Directed Energy Deposition

Investigation of the Tribological and Mechanical Properties of Electroless Ni-P-hBN Nano-Composite Coating

Enhanced Tribological Properties of CrN Coatings on Densified Surfaces of Fe-Based Porous Materials Obtained Through Powder Metallurgy and Ultrasonic Shot Peening Treatment

Formation Kinetics and Properties of CrNx/H13 Functionally Graded Coating Fabricated by PVD

Microstructure, Mechanical and Adhesive Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrided AISI 4140 Steel

The effect of substrate surface integrity on the surface properties of TiCrN coating applied via the CAE‐PVD method

Microstructure, Adhesion and Tribological Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrocarburized AISI 4140 Steel

Synthesis and Characterization of Nanocrystalline Boron-Nitride Thin Films by Ion Milling and Thermal Treatment for Tribological Coatings: An Approach to Quantifying the Growth Dynamic Process

Insights into the oxidation resistance mechanism and tribological behaviors of multilayered TiSiN/CrVxN hard coatings