Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Cyclic performance study of Q460D steel and ER55-G welds after high temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Effect of High Temperature Exposure and Strain Rate on Mechanical Properties of High-Strength Steel Rebars

DSI-based Studies of the Effects of High-temperature Aging on Local Mechanical Properties of HR3C/T92 Dissimilar Steel Welded Joint

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Cyclic Loading Test on Welded Connection of High Strength Steel Q460C

Mechanical Behavior of Q460 High-Strength Steel under Low-Cycle Fatigue Loading

Mechanical Properties of Butt Weldments Made with Q345B Steel and E5015 Electrodes at Different Temperatures

Deterioration of Mechanical Properties of Novel Constructional Steel Material at Elevated Temperatures

Mechanical properties of butt weldments made with E5515-G electrodes at high temperature

Experimental investigation of cold-formed steel material at elevated temperatures

Mechanical Performance of Artificially Rusted Q500MC Structural Steel Subjected to High Temperature

Cyclic Behavior of 460 MPa High Strength Structural Steel and Welded Connection under Earthquake Loading

Experimental study of high strength structural steel Q460D under cyclic loading

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

Longitudinal tensile test on weld metal in fusion zone at high temperature

Post-fire Mechanical Properties of Q960 Cold-Formed Thick-Walled Ultra-High-Strength Steel

Post-fire ultra-low cycle fatigue properties of high-strength steel via different cooling methods

Microstructure evolution and impact toughness variation for high strength steel multi-pass weld metals with various cooling rates

Experimental investigation on mechanical behaviours of TMCP high strength steel