Microstructure evolution and impact toughness variation for high strength steel multi-pass weld metals with various cooling rates

Wei Li,Rui Cao,Wanchao Zhu,Xili Guo,Yong Jiang,Jianhong Chen
DOI: https://doi.org/10.1016/j.jmapro.2021.03.027
IF: 5.684
2021-05-01
Journal of Manufacturing Processes
Abstract:<p>Thermally simulated experiments on high-strength weld metals were performed. Based on the results, an extended continuous cooling transformation (CCT) curve with microstructure, hardness, and impact toughness can be proposed. The microstructures, hardness, high-angle grain boundaries, impact toughness, and fracture surfaces of the weld metals treated with different cooling rates were systematically compared and analyzed. The microstructure of the original weld metal corresponds to a cooling rate of 5 °C/s and is composed of uniform granular bainite and a small amount of acicular ferrite, which is similar to that of the specimens with cooling rates of 3−30 °C/s. The increase in the cooling rates leads to the evolution of the microstructure from quasi-polygon ferrite to granular bainite. The proportion of large angle grain boundaries increases with the increasing cooling rate, which can increase the resistance of crack propagation and induce a higher impact toughness. The impact toughness at room temperature is in the range of 80–131.81 J. Various cooling rates lead to various impact toughness. Except for the cooling rate of 5 °C/s, the other cooling rates decrease the impact toughness. Moreover, at the lowest cooling rate, the decrease in the impact toughness reaches 63 %. The impact toughness at -50 °C is in the range of 34–109.86 J. The impact toughness of the weld metals without thermally simulated processes at -50 °C is 88.6 J. The reheating process decreases the impact toughness from 88.6 J to 34 J, and the decrease rate of the impact toughness at -50 °C reaches 38 %.</p>
engineering, manufacturing
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: in the multi - pass welding process, the influence of different cooling rates on the microstructure and impact toughness of high - strength steel weld metal. Specifically, the research aims to explore the microstructure evolution, hardness change and impact toughness change rules of high - strength steel weld metal under different cooling rates through thermal simulation experiments, and propose an extended continuous cooling transformation (CCT) curve to guide the parameter selection in the actual welding process and optimize the mechanical properties of weld metal, especially to improve its impact toughness. The paper mentions that by controlling the cooling rate during the welding process, the microstructure type and its distribution of weld metal can be significantly affected, which in turn affects the impact toughness of weld metal. For example, a lower cooling rate will lead to the formation of quasi - polygonal ferrite (QPF), while a higher cooling rate promotes the formation of granular bainite (GB). As the cooling rate increases, the proportion of high - angle grain boundaries (HAGBs) increases, which helps to improve the material's ability to resist crack propagation, thereby enhancing the impact toughness. However, an excessively high cooling rate may lead to the formation of martensite - austenite (M - A) constituents, and the presence of these constituents will instead reduce the impact toughness of the material. In addition, the paper also explores the influence of the cooling rate on the hardness of weld metal. It is found that as the cooling rate increases, the hardness also increases correspondingly. This is mainly due to the formation of more microstructures with higher hardness, such as granular bainite and coarse M - A constituents. However, when the cooling rate exceeds a certain value, the growth trend of hardness tends to be flat. In general, this research provides theoretical basis and technical support for optimizing the mechanical properties of high - strength steel weld metal by systematically analyzing the microstructure characteristics, hardness and impact toughness under different cooling rates.