Abstract:A 12% Cr ferritic/martensitic steel, HT-9, has been used as a primary core material for nuclear reactors. The microstructure and mechanical properties of gas tungsten arc butt welded joints of HT-9 in as-welded, and as-tempered conditions have been explored. In as-welded condition, the fusion zone (FZ) contained a fresh martensite matrix with delta (δ)-ferrite. The δ-ferrite was rich in Cr and depleted in C compared with the matrix. The heat-affected zone (HAZ) could be divided into three areas as the distance from the fusion line increased: δ-ferrite/martensite duplex zone, fully recrystallized zone, and partly recrystallized zone. Prior austenitic grains did not coarsen in the δ-ferrite/martensite duplex zone due to the newly nucleated δ-ferrite grains and incompletely ferritizing (δ-ferrite) during the welding thermal cycle. The weldment microhardness distributed heterogeneously with values above 600 HV1.0 in the HAZ and FZ and 250 HV1.0 in the base metal (BM). Solute C in the matrix, induced by the dissolution of carbide during the welding process, dominated the microhardness variation. Low toughness was observed in the FZ with a quasi-cleavage fracture tested from − 80 to 20 °C. The tensile fracture occurred in the relatively soft BM tested from 20 to 600 °C. In as-tempered condition (760 °C for 1 h), M23C6-type carbides precipitated within the martensitic laths, the lath boundaries, and the δ-ferrite/martensite interfaces. Moreover, V, Cr, Mo-rich nitrides with very small size also precipitated in the δ-ferrite/martensite interface. The tempering treatment improved the homogenous distribution of weldment hardness significantly. Tensile fracture still occurred in the BM of the weldment specimens tested from 20 to 600 °C. The impact toughness improved significantly, but the ductile–brittle transaction temperature was − 12 °C which was higher than that of the normalized and tempered (N&T) BM. δ-ferrite was considered to be one of the major factors aggravating the impact toughness in the FZ.

Study on Microstructure and Toughness of Welded Joint of 12%Cr Ferritic Stainless Steel

A Study of Microstructure and Mechanical Properties for the Autogenous Single-Pass Butt Weldment of a Ferritic/Martensitic Steel Using Gas Tungsten Arc Welding

Crucial Microstructural Features to Determine the Mechanical Properties of Welded Joints in a Cu-Containing Low-Carbon Low-Alloy Steel After Postweld Heat Treatment

Research status of welding technology of ferritic stainless steel

Microstructure and corrosion characterization of weld metal in stainless steel and low carbon steel joint under different heat input

Cold Metal Transfer Welding of Ferritic and Austenitic Stainless Steel: Microstructural, Mechanical, and Electrochemical Studies

Investigation on the weakest zone in toughness of 9Cr/NiCrMoV dissimilar welded joint and its enhancement

Microstructural and chemical dependences of fracture toughness in stainless steel welds at 4.2 K

Microstructure and Mechanical Characteristics of Dissimilar TIG Welded 9% Cr Heat-Resistant Steels Joints

Insights into microstructure evolution and fracture mechanisms of welded joints of high strength steel patchwork components

Study on Effect of Tempering Temperature on Microstructure and Properties of Super Martensitic Stainless Steel Welded Joints

Microstructure evolution and impact toughness variation for high strength steel multi-pass weld metals with various cooling rates

The Microstructure and Mechanical Properties of Welded Joints of Hot-Rolled and Post-Weld Solution-Treated Fe-12.5Mn-9.8Al-1.0C Low-Density Steel

Metallurgical and Corrosion Characterization of Austenitic Stainless Steel Welds during Post Weld Heat Treatment

Microstructure, properties and fracture failure mechanism of MAG welded joints of four types of stainless steels

Weld Formation Mechanism and Microstructural Evolution of TC4/304 Stainless Steel Joint with Cu-Based Filler Wire and Preheating

Influence of Multiple Repair Welding on Microstructure and Properties of 06Cr19Ni10 Stainless Steel

Study on Microstructure and Properties of Cold Metal Transfer and Pulse Hybrid Welded Super Duplex Stainless Steel

Improvement in Weldment of Dissimilar 9% CR Heat-Resistant Steels by Post-Weld Heat Treatment

Influence of Chemical Composition on the Mechanical and Microstructural Properties of High Strength Steel Weld Metals Submitted to PWHT

Microstructure and mechanical properties of stainless steel clad plate welding joints by different welding processes