Abstract:In order to develop high-entropy alloys with both good hot processing performance and fracture toughness, Al x CrFeNiCu1.5(x=0, 0.2, 0.4, 0.6, 0.8) alloys were designed and prepared. The alloy was firstly hot rolled by a twin-roll rolling device, and then the hot processing performance of the alloy under different Al contents was explored, whether the fracture toughness was at an ideal level, and if so, why it was at an ideal level. The results showed that the phase composition after hot rolling and annealing were two phases (face-centered cubic FCC and body-centered cubic BCC). With the increase of Al content, the FCC phase gradually transformed into BCC phase, and the increase of BCC phase led to the decrease of plasticity, which led to the decrease of hot processing performance. With the increase of Al content, the average fracture toughness value increased first and then decreased. Among them, the Al0.2CrFeNiCu1.5 and Al0.4CrFeNiCu1.5 alloys had the relatively better fracture toughness, which was because that the alloys had the appropriate proportion of FCC and BCC phases, and the strength and plasticity could achieve an ideal match. Among these alloys, the Al0.2CrFeNiCu1.5 alloy had the relatively better hot processing performance and ideal fracture toughness, and its average fracture toughness was 35.71 MPa·m1/2. And compared with Al0.2CrFeNiCu1.5 alloy, the Al0.4CrFeNiCu1.5 alloy had the worse hot processing performance, but it yielded the best fracture toughness, with an average value of 45.27 MPa·m1/2. In the crack propagation morphology, we found the main crack terminated at the notch upper part for the Al0.2CrFeNiCu1.5 alloy, suggesting that the material has good plasticity. And we also found crack multiple deflections and secondary cracking for the Al0.4CrFeNiCu1.5 alloy, which was helpful to improve the fracture toughness.

Effects of multi-scale precipitated phases on the toughness of FeCrAl alloy investigated by varying cooling mode and RE doping

The Effects of Refractory Elements on Mechanical Properties in CoCrNiFe Concentrated Solid Solution Alloys Across Different Temperatures

Toughness under Different Rolling Processes in Ultra Purified Fe–17wt% Cr Alloy Steels

Effects of Fe on microstructure and mechanical properties of CoCrNiFeAl multi-principle elements alloys

Hot processing performance and fracture toughness control of Al CrFeNiCu1.5 (x = 0, 0.2, 0.4, 0.6, 0.8) high entropy alloys

Control of Laves Precipitation in a FeCrAl-based Alloy Through Severe Thermomechanical Processing

Modification and refinement of Fe-containing phases, mechanical properties and strengthening mechanisms in Al–Fe alloys via Cr alloying and continuous rheo-extrusion

The Effect of Cooling Rate on Microstructure and Mechanical Properties of the Zr-4Hf-3Nb (wt%) Alloy

Influence of Zr on grain orientation, texture, and mechanical properties in hot- and warm-rolled FeCrAl alloys

Effect of Cr on the phase transformation and interphase nanoprecipitation behaviours of high-strength microalloyed steels

Effects of Fe on L12 phase precipitation and mechanical properties in Al0.3CrFeCoNi high-entropy alloy

The role of the ω phase on the microstructure evolution of precipitation and mechanical property in Ti-3Al-5Mo-4Cr-2Zr-1Fe

Influence of Cold-Rolling Reduction on Microstructure and Tensile Properties of Nuclear FeCrAl Alloy with Low Cr and Nb Contents

Effect of Fe-Rich Phases on Fracture Toughness of High Strength Al-Zn-Mg-Cu Alloy

Importance of cold rolling and tempering on the microstructure evolution, precipitation behavior and mechanical responses of 9Cr3Co3W1Cu ferritic/martensitic steel

Effects of annealing at 800 and 1000 °C on phase precipitates and hardness of Al7Cr20Fe Ni73− alloys

The Effects of Microstructure Refinement and Coincidence Site Lattice Boundaries on the Plasticity of FeCrAlY Alloys

Effects of the cooling rate on mechanical properties and microstructure of near- α Ti-6Al-3Zr-2Nb-Mo alloy

An excellent synergy in yield strength and plasticity of NbTiZrTa 0.25 Cr 0.4 refractory high entropy alloy through the regulation of cooling rates

Effects of cooling manner on Laves phase precipitation and mechanical properties of Al modified super ferritic stainless steels

Regulating the dissolution of brittle nano-precipitated phase in FeCrAl alloy by pulse current to repair aging properties