Abstract:In this study, the recycled Al-Mg-Mn-Fe alloys having different Fe levels (0.1%, 0.5%, and 0.8%) were successfully developed by applying squeeze casting without heat treatment. Optical and scanning electron microscopy, synchrotron X-ray tomography and radiography, X-ray diffraction, and tensile tests combined with thermodynamic calculations were used to study the correlation between the microstructural evolution and mechanical properties. The results showed that for the alloys with an applied pressure of 75 MPa, as the Fe increase from 0.1% to 0.8%, the yield strength (YS), and ultimate tensile strength (UTS) increased from 122 MPa and 244–146 MPa and 289 MPa, and elongation decreased from 34% to 12%. Even though Fe additions increased the volume fraction of Fe-rich intermetallic phases, it significantly increased the UTS and YS. The synchrotron X-ray tomography and deep-etched results both show that the 3D morphology changed from individual Chinese-script to interconnected plate-like. The 3D morphology of 0.8Fe alloy clearly demonstrate that the hole partially or whole penetrated the entire rectangle-shaped Al6(FeMn) phases, which is due to the close-packed plane growth. In-situ synchrotron X-ray radiography results showed the facet growth behaviour of Al6(FeMn) in 0.8Fe alloys during solidification with a long needle-like shape. The size of primary Al6(FeMn) phases decreases, whereas their number increases with increasing cooling rate. Moreover, the applied pressure was beneficial in refining the size of α-Al grains and Fe-rich phases and reducing the volume fraction of pores, thus contributing to the improvement of strength and elongation. The in-situ tensile test results indicated that the crack initiated in the Fe-rich phases and pores, and the slip lines were blocked by the Fe-rich phases resulting in the strengthening of the secondary phases.

Effect of Fe-Rich Phases on Fracture Toughness of High Strength Al-Zn-Mg-Cu Alloy

Revealing the influence of Fe on Fe-rich phases formation and mechanical properties of cast Al-Mg-Mn-Fe alloys

Synchrotron X-ray tomography investigation of 3D morphology of intermetallic phases and pores and their effect on the mechanical properties of cast Al-Cu alloys

Grain Refinement Enhanced Tensile Strength, Fracture Toughness and Fatigue Crack Propagation Resistance of a High Zn-Containing Al-Zn-Mg-Cu Alloy

Dependence of Fracture Toughness on Multiscale Second Phase Particles in High Strength Al Alloys

Fracture toughness of Ti 2 AlNb alloy with different Al content: intrinsic mechanism, extrinsic mechanism and prediction model

Evolution of the Second-Phase Particles and Their Effect on Tensile Fracture Behavior of 2219 Al-xCu Alloys

Effect of Fe content on low cycle fatigue behavior of squeeze cast Al-Zn-Mg-Cu alloys

Multi-scale iron-rich phases induce fine microstructures in Al-Zn-Mg-Cu-Fe alloys

Fracture toughness of Ti2AlNb alloy with different Al content: intrinsic mechanism, extrinsic mechanism and prediction model

Influence of Cr and Yb alloying on the microstructures and fracture characteristics of Al-Zn-Mg-Cu-Zr alloy

Effect of Fe, Mn, Ce on the Microstructure and Mechanical Properties of Al-Mg and Al-Mg-Si Die Casting Alloys

Effects of multi-scale precipitated phases on the toughness of FeCrAl alloy investigated by varying cooling mode and RE doping

The Alloying Strategy to Tailor the Mechanical Properties of θ-Al13Fe4 Phase in Al-Mg-Fe Alloy by First-Principles Calculations

Effects of Aluminum on Microstructure and Compressive Properties of Al-Cr-Fe-Ni Eutectic Multi-Component Alloys

Hot processing performance and fracture toughness control of Al CrFeNiCu1.5 (x = 0, 0.2, 0.4, 0.6, 0.8) high entropy alloys

The characterization of Fe-rich phases in a high-pressure die cast hypoeutectic aluminum-silicon alloy

Multi-alloying effect of Ti, Mn, Cr, Zr, Er on the cast Al-Zn-Mg-Cu alloys

Fracture Behavior and Structural Transition of Ni46Mn33Ga17Cu4−Zr Alloys

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Study on the effect of enhanced magnesium and copper contents on microstructure and property of Al-Zn-Mg-Cu alloys with high zinc element content during fabrication processes