Effects of annealing at 800 and 1000 °C on phase precipitates and hardness of Al7Cr20Fe Ni73− alloys

Chang-jun WU,ZHOU Chen,Jiao-feng ZENG,LIU Ya,TU Hao,Xu-ping SU,Chen ZHOU,Ya LIU,Hao TU

DOI: https://doi.org/10.1016/s1003-6326(21)65534-6

IF: 3.752

2021-03-01

Transactions of Nonferrous Metals Society of China

Abstract:The effects of Fe content on the microstructure, phase constituents and microhardness of the as-cast, 800 °C- or 1000 °C-annealed Al7Cr20Fe x Ni73−x (x=13−66) alloys were investigated. Not all these alloys are composed of the single FCC phase. The BCC and B2 phases are found. It is confirmed that the BCC phase in the Al7Cr20Fe66Ni7 alloy is transformed from the FCC phase at about 900 °C during cooling. While in the 800 °C-annealed Al7Cr20Fe60Ni13 alloy, the FCC phase is stable and the hardness decreases. After annealing at 1000 °C, for the precipitation of the B2 particles, the Al content in the FCC phase decreases, which results in decreasing of the alloy hardness. Moreover, after annealing at 800 °C, a small amount of Al-rich B2 particles precipitate at the phase boundary and some nanocrystal BCC phase precipitates in the FCC matrix, which increases the hardness of the Al7Cr20Fe x Ni73−x (x=41−49) alloys. These results will help to the composition design and processing design of the Al−Cr−Fe−Ni based high-entropy alloys.

metallurgy & metallurgical engineering