Abstract:The use of metal-coated ceramic powders not only effectively enhances the wettability of the metal–ceramic interface but also promotes a more uniform microstructure in Ti(C,N)-based cermets, which is advantageous for improving their mechanical properties. In this study, ultrafine Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders were synthesized via the spray-drying-in-situ carbothermal reduction method. Subsequently, Ti(C,N)-based cermets were effectively fabricated using the as-prepared ultrafine Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders. The impact of reaction temperature, heating rate, and isothermal time on the phase and microstructure of prepared powders was analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Additionally, the microstructure of the as-sintered cermets was experimentally investigated. The findings reveal that the complete reduction of Co and Ni metal salts, pre-coated on the surface of (Ti,W,Mo,Ta)(C,N) particles, can be achieved through rapid heating (10 °C/min) in a specific temperature range (600–1000 °C) with an isothermal time of 3 h at a lower reduction temperature (1000 °C). The synthesized powders have only two phases: the (Ti,W,Mo,Ta)(C,N) phase and Co/Ni phase, and no other heterogeneous phases were observed with an oxygen content of 0.261 wt.%. Notably, the conventional core–rim structure was not dominant in the cermets obtained from the prepared Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders. Moreover, the heterogeneous segregation effect of the Co/Ni coating on the ultrafine powder particles resulted in a finer microstructure than the traditional cermets with the same composition. However, the grain size is mainly in the range of 0.5–0.8 μm. The weaker residual stresses at the core and rim interfaces and the finer particle distributions could theoretically enhance the toughness of Ti(C,N)-based cermets, simultaneously.

The morphology regulating effect of cobalt acetate on the vacuum carbothermal synthesis of β-SiC powder

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Effect of Catalyst on the Preparation of Silicon Carbide Whiskers from Silica and Carbon

Synthesis of nanocrystalline silicon carbide powders

Synthesis of SiC@SiO2 Nanocables Via a Catalyst-Free Carbothermal Reduction Method

Improving the strength and oxidation resistance of phenolic resin derived pyrolytic carbons via Cu-catalyzed in-situ formation of SiC@SiO2

Controlled growth of SiC crystals in combustion synthesis

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

EFFECT OF AL(2)O(3) AND SIC CONTENT IN PACK CEMENTATION POWDERS ON THE MICROSTRUCTURE OF SIC COATINGS ON HTR GRAPHITE SPHERES

The Fe-Incorporation Effects on the Structural Evolution of SiOC Ceramics

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Highly active Co/SiC catalysts with controllable dispersion and reducibility for Fischer-Tropsch synthesis

Graphitisation and microstructure transformation of carbon-encapsulated cobalt nanoparticles synthesised by chemical vapour deposition using alumina powder as catalytic support

Microstructure Evolution of Cobalt Coating Electroless Plated on SiC Whisker During Electroless Plating and Heat Treatment

Uniformity Dispersive, Anti-Coking Core@double-Shell-structured Co@SiO2@C: Effect of Graphitic Carbon Modified Interior Pore-Walls on C5+ Selectivity in Fischer-Tropsch Synthesis

Preparation of Ultrafine Co- and Ni-Coated (Ti,W,Mo,Ta)(C,N) Powders and Their Influence on the Microstructure of Ti(C,N)-Based Cermets

Preparation Of Al2o3-Sic Composite Powder From Kyanite Tailings Via Carbothermal Reduction Process

Fabrication of carbon-coated cobalt nanoparticles by the catalytic method

Temperature field regulation and growth mechanism of SiC fiber during microwave synthesis with catalyst assistance