Extraction of potassium from K-feldspar via the CaCl2 calcination route
Bo Yuan,Chun Li,Bin Liang,Li Lü,Hairong Yue,Haoyi Sheng,Longpo Ye,Heping Xie
DOI: https://doi.org/10.1016/j.cjche.2015.06.012
IF: 3.8
2015-09-01
Chinese Journal of Chemical Engineering
Abstract:The extraction of potassium from K-feldspar via a calcium chloride calcination route was studied with a focus on the effects of the calcination atmosphere, calcination temperature and time, mass ratio of CaCl2 to K-feldspar ore and particle size of the K-feldspar ore. The results demonstrated that a competing high-temperature hydrolysis reaction of calcium chloride with moisture in a damp atmosphere occurred concurrently with the conversion reaction of K-feldspar with CaCl2, thus reducing the amount of potassium extracted. The conversion reaction started at approximately 600°C and accelerated with increasing temperature. When the temperature rose above 900°C, the extraction of potassium gradually decreased due to the volatilization of the product, KCl. As much as approximately 41% of the potassium was volatilized in 40min at 1100°C. The mass ratio of CaCl2/K-feldspar ore significantly affected the extraction. At a mass ratio of 1.15 and 900°C, the potassium extraction reached 91% in 40min, while the extraction was reduced to only 22% at the theoretical mass ratio of 0.2. Optimal process conditions are as follows: ore particle size of 50–75μm, tablet forming pressure of 3MPa, dry nitrogen atmosphere, mass ratio of CaCl2/ore 1.15:1, calcination temperature of 900°C, and calcination time of 40min. The XRD analysis revealed that a complex phase transition of the product SiO2 was also accompanied by the conversion reaction of K-feldspar/CaCl2. The SiO2 product formed at the initial stage was in the quartz phase at 900°C and was gradually transformed into cristobalite after 30min.
engineering, chemical