Abstract:To improve the potassium availability of feldspar at ordinary temperatures, the mechanical grinding and addition of sodium hydroxide/salts were employed to study the effects of mechanical activation and strong alkali addition on particle characteristics, water-soluble potassium, and the available potassium of feldspar. A laser particle size analyzer was utilized for the direct determination of particle size distribution (PSD) using ground samples. The Brunauer-Emmett-Teller (BET) method was employed for specific surface areas. X-ray diffraction (XRD) was employed for structural characterization, scanning electron microscopy (SEM) for morphology exploration, and energy dispersive spectroscopy (EDS) to determine the chemical composition of potassium feldspar powder. The results revealed that the mechanical activation of potassium feldspar could reduce the particle size and produce agglomerated nanoparticles in the later period. The addition of NaOH and sodium salt did not cause agglomeration, and NaOH dissolved the nanoparticles. The water-soluble potassium content of feldspar in each treatment increased during mechanical grinding, from 21.64 mg kg-1 to 1495.81 mg·kg-1, by adding NaOH 5% weight of potassium feldspar powder and to 3044.08 mg·kg-1 by adding NaOH 10% weight with effects different from those of mechanical shaking. By comparison, only 162.93 mg·kg-1 water-soluble potassium was obtained by adding NaOH 5% weight. The dissolved potassium in the former case was significantly higher than in the latter, and the addition of NaOH and sodium salts significantly enhanced the water-soluble potassium contents due to ion exchange. Furthermore, the addition of sodium hydroxide improved the water-soluble potassium due to its mechanochemical action on potassium feldspar. The mechanical energy changed the crystal structure of potassium feldspar, explaining the increase in available potassium. The addition of sodium salts did not promote change in the feldspar's structure, thereby did not raise the available potassium content. The reason for this was related to the mechanochemical action on sodium hydroxide and feldspar, which could promote the dissolution of fine particles, thereby incrementing the available potassium.

Evolution of mineral phases and microstructure of high efficiency Si–Ca–K–Mg fertilizer prepared by water-insoluble K-feldspar

Activate nutrients access to plants as multiphase slow-release fertilizers by sintering reaction in K2O–MgO–Al2O3–SiO2 system using K-feldspar as a major source

Thermal Preparation and Application of a Novel Silicon Fertilizer Using Talc and Calcium Carbonate as Starting Materials

Preparation of potassium sulfate and zeolite NaA from K-feldspar by a novel hydrothermal process

A silicon–potash fertilizer prepared from magnesium slag and how it can improve soil fertility and agronomic performance

Effect of manganese salts on recovery of potassium from K-feldspar by means of a calcination reaction in the chloride salts-calcium carbonate system

Review on K-Feldspar Mineral Processing for Extracting Metallic Potassium as a Fertilizer Resource

A novel process for one-step preparing potassium-containing fertilizer using red mud or CFA synergistic extraction of alumina

Mechanism of Potassium Release from Feldspar by Mechanical Activation in Presence of Additives at Ordinary Temperatures

Extraction of potassium from K-feldspar via the CaCl2 calcination route

Sustainable application of sodium removal from red mud: Cleaner production of silicon-potassium compound fertilizer

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Sustainable and Clean Utilization of Coal Gangue: Activation and Preparation of Citrate-Soluble Silicon Fertilizer

[Study on the Influence of Mineralizer on the Preparation of Calcium Aluminates Based on Infrared Spectroscopy]

Research on the mechanism of sodium separation in bauxite residue synergy preparation of potassium-containing compound fertilizer raw materials by the hydrothermal method

Hydrothermal extraction of potassium from potassic quartz syenite and preparation of aluminum hydroxide

Study on the integrated roasting process of kalsilite ore-CaCl2·2H2O system

Mechanochemical activation of phlogopite to directly produce slow-release potassium fertilizer

Crystalline phase analysis and phosphorus availability after thermochemical treatment of sewage sludge ash with sodium and potassium sulfates for fertilizer production

Hydrothermal alkaline synthesis and release properties of silicon compound fertiliser using high-ash coal slime

Study of phase transformation of calcium silicate using desert sand as raw materials