Abstract:According to ASTM 403C, initial setting time of concrete is measured based on penetration resistance of mortar sieved from concrete and it is considered as the time taken to achieve a penetration resistance of 3.5MPa which is an arbitrary value. The main objective of this research is to find a test method to obtain a realistic initial setting time value in order to plan the placing of concrete to prevent formation of cold joints which can affect the performance of the structure. Mechanical properties (tensile strength and shear strength) at a purposely made cold joint was evaluated by testing concrete cubes cast in two layers with different time lags between placing of concrete in the two layers. Point of change of each strength parameter with respect to time lag was identified and corresponding time range was identified as the initial setting time range. Standard penetration resistance test was also carried out and with the use of penetration resistance vs. elapsed time graph, corresponding penetration resistance value was also identified. Although this new method is effective to identify the initial setting time of concrete, it is not possible to use as a field test since it a time consuming and complicated test. Therefore, an attempt was made to introduce a simple field test method. Ultrasonic pulse velocity is used to measure properties of hardened concrete, because pulse velocity of a concrete sample depends on its elastic modulus and density. Since properties of fresh concrete such as elastic modulus changes with time, the ultrasound pulse velocity was used to monitor the change of stiffness of fresh concrete with time. Based on the test results of the experimental investigations, it was found that the more realistic initial setting time of concrete is the onset time of the penetration resistance of mortar measured in the standard penetration test. This was further verified by a simple qualitative field test where the initial setting time is considered as the latest time that a vibrating poker can be inserted into the concrete and removed without leaving a significant trace.

Assessing setting times of cementitious materials using semi-adiabatic calorimetry

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

The Application of Acoustic Emission Technique to Monitor the Early Setting Process of Cement Pastes

A new method to determine initial setting time of cement and concrete using plate test

Setting Times of Early-Age Mortars Determined from Evolution Curves of Poisson's Ratio.

Detection of setting time in cement hydration using patch antenna sensor

A Mathematical Model for the Electrical Resistivity of Cement Paste at Early Ages Considering the Partially Saturated State

The Influence of the Acceleration Admixture Type and Composition of Cement on Hydration Heat and Setting Time of Slag Blended Cement

Programmatic Data Analysis for Quantitative Isothermal Heat Flow Calorimetry of Cementitious Materials

Evaluation of initial setting time of fresh concrete

On the relation of setting and early-age strength development to porosity and hydration in cement-based materials

Use of calorimetry and thermal analysis to assess the heat of supplementary cementitious materials during the hydration of composite cementitious binders

Determination of water permeability for cementitious materials with minimized batch effect

A new method for measuring initial setting time of roller compacted concrete

Experimental Study of Effects of Factors on RCC Setting Times

Setting Time and Strength Monitoring of Alkali-Activated Cement Mixtures by Ultrasonic Testing

Comparison of the Calcium Carbide Method and Darr Drying to Quantify the Amount of Chemically Bound Water in Early Age Concrete

Long-Term Capillary Imbibition of Mortars with Slag and Fly Ash

Effect of Temperature on the Early-age Hydration and Setting Behaviour of Mixes Containing GGBS

Setting Times of Early-Age Mortars Determined from Evolution Curves of Poisson’s Ratio

Measurements of Thermal Conductivity of LWC Cement Composites Using Simplified Laboratory Scale Method