Abstract:Powder sintering and in–situ foaming are the primary treatments for the preparation of glass ceramic foams from solid wastes. However, variables such as crystallization and viscosity, which are difficult to regulate at high temperatures. Herein, a novel technology based on alkali activation–crystallization strengthening was developed for the fabrication of glass ceramic foams with hierarchical pores. Vitrified municipal solid waste incineration (MSWI) ashes as the main calcium and aluminum source and secondary aluminum ash (SAA) as a foaming agent were foamed in NaOH solution at room temperature. The effects of solid–liquid ratio and NaOH concentration on the pore structure, individual foam force, phase evolution and physical properties were investigated, including crystallization kinetics and hierarchical pore formation mechanism. The results indicated that the solid–liquid ratio decreased from 60:40 to 40:60, making the pore wall thin and eventually disappear. The pore size in the range of 0–1 mm reaches 99.5% in 3 mol/L NaOH sample, with the lowest mean size of 0.34 mm. The crystallization kinetics parameters of the basic glass at 5–20 K/min showed that grains were primarily precipitated as three–dimensional at 5 K/min, resulting in micropores. The prepared samples exhibit high porosity (79.23–88.35%), adequate compressive strength (0.36–5.55 MPa) and a bulk density of 0.68–0.76 g/cm3. This work develops the function of SAA as a foaming agent at room temperature, as well as a new idea for the preparation of glass ceramic foams from solid waste containing glass phase or needing vitrification.

Foaming mechanism of polishing porcelain stoneware tile residues via adding C, Al and Si powder

The cause of foaming in polishing porcelain stoneware tile residues during sintering: Interface corrosion of Silicate-SiC

Fabrication of foamed ceramics with enhanced compressive strength and low thermal conductivity via a simple route

High-strength building materials by recycling porcelain stoneware waste with aluminum powder

Foaming Inhibition of SiC-containing Porcelain Ceramics by Using Si Powders During Sintering

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Synthesis of a foam ceramic based on ceramic tile polishing waste using SiC as foaming agent

Effects of magnesium oxychloride and silicon carbide additives on the foaming property during firing for porcelain ceramics and their microstructure

Effect of silicon carbide particle size and CaO content on foaming properties during firing and microstructure of porcelain ceramics

Effect of silicon carbide additive on microstructure and properties of porcelain ceramics

Preparation of ceramic foams from ceramic tile polishing waste and fly ash without added foaming agent

Preparation and characterization of ceramic foams mainly containing extracted titanium residues and silica tailings

Effect of porcelain polishing waste additive on properties and corrosion resistance of ceramic foams produced from zeolite

Novel Glass Ceramic Foams Materials Based on Polishing Porcelain Waste Using the Carbon Ash Waste As Foaming Agent

Effects of Ammonium Molybdate Additive and Sintering Temperature on the Properties of Foam Ceramics Based on Ceramic Tile Polishing Waste

Preparation and characterization of foam ceramics from red mud and fly ash using sodium silicate as foaming agent

Preparation of foam ceramics from solid wastes: a study on the relationship between firing regime and properties by grey system theory

Preparation of Self-Coating Al2O3 Bonded SiAlON Porous Ceramics Using Aluminum Dross and Silicon Solid Waste under Ambient Air Atmosphere

Effect of holding time on the properties of porous ceramics with high-volume polished slag and its pore structure characteristics

Design and Formulation of Polyurethane Foam Used for Porous Alumina Ceramics

A novel approach for preparing glass ceramic foams from MSWI fly ash: foaming characteristics and hierarchical pore formation mechanism