Abstract:Large-size pure titanium ingots melted by single electron beam cold hearth melting (EBCHM)) could be rolled into large-width and heavy-weight titanium strip coils using short process without forging. It is crucial to study the large-span refinement mechanism from highly coarse grains, whose sizes are in the order of ∼cm, to micronmeter. In this study, the recrystallization mechanism and texture evolution of pure titanium with a size of 1570 × 200 × > 8000 mm was investigated by multi-pass simulated rolling and experimental rolling. The results indicated the hot deformation can result in marked reduction in grain size of the as-cast grain, from 3 to 5 cm to 17–23 μm. The discontinuous dynamic recrystallization (DDRX) mechanism of a pure titanium ingot during direct multi-pass hot deformation causes the reconstruction of as-cast microstructure and refinement of hot rolling microstructure. Furthermore, DDRX occurred, during hot deformation, and was accompanied with weakening of deformation texture. Raising the initial hot deformation temperature results in a modification of the texture type of the {0001} crystal plane. The strength of the texture experiences a decrease initially and then eventually an increase. This alteration in strength is inversely related to the degree of dynamic recrystallization. Based on the simulated rolling experiment, the results of experimental rolling also found the coarse as-cast grains was broken and reconstructed. It has strength (average yield strength: 334 MPa, ultimate tensile strength: 371 MPa), ductility (total elongation: 30 %). Such a combination of mechanical properties makes the hot rolling plate a potential choice for sheet practical application.

Microstructure Evolution Through Cryogenic Rolling of Ultra-High Purity Titanium Produced by Electron Beam Melting

Microstructural Evolution and Mechanical Properties of Ultrafine‐Grained Ti Fabricated by Cryorolling and Subsequent Annealing

Analysis of Microstructure, Texture Evolution, and the Mechanism of Grain Refinement of Commercially Pure Titanium During Cold Rolling: Experiment and Simulation

Microstructure Evolution and Strengthening Mechanism of Ultrarefine-grained Pure Titanium Fabricated by Repeated Rolling

Work Hardening Behavior and Microstructure Evolution of a Cu-Ti-Cr-Mg Alloy during Room Temperature and Cryogenic Rolling

Discontinuous dynamic recrystallization behavior and texture evolution of large-size pure titanium flat ingot via electron beam cold hearth melting during short process direct hot rolling

Effect of Direct Rolling Process on Microstructure and Mechanical Properties of the Electron Beam Cold Hearth Melting Ti-6Al-4V Alloy

Static Recrystallization Behavior and Texture Evolution during Annealing in a Cold Rolling Beta Titanium Alloy Sheet

Effects of Annealing on Microstructure and Mechanical Properties of Nano-Grained Titanium Produced by Combination of Asymmetric and Symmetric Rolling

Microstructure Evolution and Mechanical Properties of Pure Ti Alloy Sheet Fabricated by Double-Side Corrugated Rolling

Cryorolling impacts on microstructure and mechanical properties of AISI 316 LN austenitic stainless steel

Microstructure and Mechanical Properties of Asymmetrically Rolled High-Purity Titanium Ultra-Thin Strips

Microstructure and texture evolutions of 310S austenitic stainless steel after cryogenic rolling and subsequent annealing: X-ray and electron backscatter diffraction studies

Effect of Deep-Cooling Rolling Deformation on the Microstructure and Mechanical Properties of an Al-4.5Cu-1.5Mg-0.6Mn-0.2Ti Alloy

Microstructure Evolution and Mechanical Properties of Ti-15-3 Alloy During Cold-Rolling

Effect of Microstructure Evolution on Mechanical Properties of a TiZrAlB Alloy Rolled by Different Processes

Effect of Cold Rolling Process on Microstructure and Mechanical Properties of High Strength Β Titanium Alloy Thin Sheets

Mechanical Properties and Microstructure of a Ti-6Al-4V Alloy Subjected to Cold Rolling, Asymmetric Rolling and Asymmetric Cryorolling

Evolution of Microstructural and Mechanical Properties during Cold-Rolling Deformation of a Biocompatible Ti-Nb-Zr-Ta Alloy

Evolutions of the microstructures and mechanical properties of TC18 titanium alloy processed by hot-rolling in β single-phase region

Effect of Thermal Annealing on the Microstructure, Mechanical Properties and Residual Stress Relaxation of Pure Titanium after Deep Rolling Treatment