Abstract:In this study, AA7075 sheets were processed by cryorolling and room-temperature rolling respectively, and subsequent aging. The microstructure evolution and mechanical properties of AA7075 sheets were investigated by hardness measurements, tensile tests, X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Results show that with the rolling reduction ratio of 80%, the room-temperature rolled samples had massive edge cracks, while the cryorolled samples were in good shape and without any cracks. The improved ductility of materials in cryogenic environments, the reduced precipitation and the absence of shear bands in sheets during cryorolling contributed to the reduced edge cracks. Compared to solution treated samples, the yield strength and ultimate tensile strength of cryorolled samples were increased by 155% and 44%, respectively, and the elongation decreased as a loss, which is obviously better than that of room-temperature rolled samples. After the subsequent aging treatment, the strength and ductility of the rolled samples were simultaneously improved, the yield strength of cryorolled + peak-aged sample was increased by 44 MPa and the elongation was increased by 68% compared with those of the cryorolled samples. Compared with room-temperature rolled + peak-aged samples, the strength of cryorolled + peak-aged sample was higher, and the elongation to failure and uniform elongation were increased by 58% and 72%, respectively. Numerous nanosized GP zones and η' phases were precipitated after aging, and the precipitation strengthening is the main contributor to the strength enhancement of the samples after aging. The improved ductility of cryorolled + peak-aged samples is mainly due to the combined effect of dislocation annihilation, uniform deformation and fine precipitates in them.

Study of mechanical characteristics and strengthening mechanism of AA5154 during cryogenic rolling

Influence of alloy chemistry on the deformation behaviour and anisotropic properties of aluminium ultra-fine-grained thin sheets

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

Microstructure evolution, mechanical response, and corrosion resistance for a 2195 Al-Li alloy under different rolling reductions during cryorolling

Work Hardening Behavior and Microstructure Evolution of a Cu-Ti-Cr-Mg Alloy during Room Temperature and Cryogenic Rolling

Improving Precipitation in Cryogenic Rolling 6016 Aluminum Alloys during Aging Treatment

Effect of cryogenic rolling on the microstructure and texture of CuCrZr alloy

Effects of cryorolling, room temperature rolling and aging treatment on mechanical and corrosion properties of 7050 aluminum alloy

Effect of Cryorolling and Ageing on the Microstructure and Mechanical Properties of Al 7085 Alloy

Microstructure and mechanical properties of ARB-processed AA1050/AA5052 multilayer laminate sheets during cryorolling

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Deformation mechanism and mechanical properties of a CoCrFeNi high-entropy alloy via room-temperature rolling, cryorolling, and asymmetric cryorolling

Edge-crack free and high mechanical properties of AA7075 sheets by using cryorolling and subsequent aging

Effect of Cryogenic Time on Microstructure and Properties of TRCed AZ31 Magnesium Alloy Sheets Rolled during Cryogenic Rolling

Experimental and computational investigation of fracture toughness of cryo-rolling processed Al-6082 alloys

Microstructure and Mechanical Properties of AA1050/AA6061 Laminated Composites Fabricated through Three-Cycle Accumulative Roll Bonding and Subsequent Cryorolling

Effect of heat treatment on the microstructure and mechanical properties of cryogenic rolling 2195 Al–Cu–Li alloy

Effect of Cold Rolling and Cryogenic Treatment on the Microstructure and Mechanical Properties of Fe–32Ni Alloy

Recrystallization behavior and texture evolution during annealing of cryogenic-rolled 3003 aluminum alloy

Effects of cryogenic treatment on microstructure and mechanical properties of AZ31 magnesium alloy rolled at different paths

Effects of annealing treatment on mechanical properties of 8011 aluminum alloy after cryogenic rolling