Twins and β 0 precipitation effects on the lamellar degradation in TNM alloy during creep

yuqing Li,Hongchao Kou,Yonghao Yu,Zilong Zhang,Yarong Wang,Jinshan Li

DOI: https://doi.org/10.2139/ssrn.4868907

IF: 4.075

2024-08-23

Intermetallics

Abstract:In this paper, the microstructure instability of the TNM alloy during creep at 800 °C under 150 MPa and 250 MPa was investigated. The results indicate that, both β 0 precipitation (inside lamellae) and primary γ twins formation are initiated during the second stage of creep. Compared to low creep stress conditions (150 MPa), high creep stress conditions (250 MPa) accelerate the initiation of the third stage of creep, inducing the precipitation of ω 0 phase and secondary twins. The nanoscale ω 0 particles formed inside β 0 or at the interface of the β 0 /β 0 . The intersection of secondary γ twins and α 2 lamellae leads to stress concentration and dislocation accumulation, providing nucleation points for β 0 phase and promoting the precipitation of β 0 within α 2 lamellae. The precipitation of the secondary γ twin introduces a unit dislocation of 1/3 [111]γ in the (111) atomic planes, promoting the movement of adjacent atomic planes within the (111) atomic planes. The 1/3 [111]γ dislocations will dissociate into two partial dislocations via 1/3 [111]γ→1/4 [11 1 ̅ ]γ T +1/9 [0 1 ̅1 ]γ M . The adjacent atomic planes of the γ matrix and secondary γ twin can transformation to β 0 through shear along 1/9 [0 1 ̅1 ]γ M and 1/4 [11 1 ̅ ]γ T , respectively. The size and content of β 0 phase significantly increase in the third stage of high creep stress, accelerating the decomposition and fragmentation of the α 2 lamellae, leading to rapid creep failure.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering