Microstructure and Creep Performance of a Multicomponent Co-Based L1 2-Ordered Intermetallic Alloy
E. Lass,F. Xue,D. Seidman,D. Dunand,F. Long,D. Chung,S. Baik
DOI: https://doi.org/10.2139/ssrn.3499089
2019-12-05
Abstract:The chemistry, thermodynamics and mechanical properties of the L1<sub>2</sub>-ordered Co<sub>3</sub>(Al,W) γ'-phase are crucial for understanding γ(f.c.c.)/γ'(L1<sub>2</sub>) cobalt-based superalloys. A single-phase γ'(L1<sub>2</sub>) alloy with the composition Co-30Ni-11Al-5.5W-4Ti-2.5Ta-0.10B (at.%) and a γ'-solvus temperature of 1268°C was recently identified using a Calphad-methodology. Scanning and transmission electron microscopy reveals that the single-phase microstructure is stable at 900 and 1000 °C for 1000 h and at 1100 °C for 168 h, without other phases being observed, resulting in similar levels of microhardness for all annealing temperatures. Atom-probe tomography confirms the presence of a single-phase γ'(L1<sub>2</sub>)-microstructure with a composition of (Co,Ni)<sub>3</sub>(Al,W,Ti,Ta,B). Grain boundaries exhibit depletion of Co, Ni, W and Ta and enrichment of Al and B. A remarkable yield stress anomaly is observed, with the yield strength increasing from ~300 to ~700 MPa from room temperature to 800°C, which is stronger than Co<sub>3</sub>(Al,W)(L12) and Ni<sub>3</sub>Al(L1<sub>2</sub>). The creep tests at 850 and 950 °C display power-law behavior with a stress exponent of n = 3.7 and an activation energy for L26 of Q<sub>n</sub> = 497 kJ/mol, similar to that of single-phase Ni<sub>3</sub>Al(L1<sub>2</sub>) compound (Q<sub>n</sub> = 406-421 kJ/mol).
Engineering,Materials Science