Creep Behavior and Related Phase Precipitation of a Creep-Resistant Y2O3-bearing High Nb Containing TiAl Alloy
Zhenquan Liang,Shulong Xiao,Qingchao Li,Xinyi Li,Dazhao Chi,Yunfei Zheng,Lijuan Xu,Xiang Xue,Jing Tian,Yuyong Chen
DOI: https://doi.org/10.1016/j.matchar.2023.112767
IF: 4.537
2023-01-01
Materials Characterization
Abstract:In this study, a creep-resistant Ti-45Al-6Nb-2.5V-0.15Y2O3 alloy was developed, and the microstructure char-acteristics at different creep stages at 850 degrees C under 200 MPa was investigated in detail. The results show that creep deformation of this alloy depends not only on dislocation slip and climb of gamma phase, but also on alpha 2 phase due to the activation of 2 c -> + -> a slip system. Meanwhile, 1/6 < 112]{111} twinning systems are initiated, gradually leading to twin intersections. Then, the interactions among dislocation, twin boundary and Y2O3 particle cause creep hardening. Whereas the occurrence of dynamic recrystallization softens the alloy. When entering the accelerated creep stage, the surface damage caused by oxidation and the bulk damage caused by void nucleation will result in the increase of creep rate until fracture. In addition, metastable TiAl2 phase with ZrGa2 structure nucleates on the dislocation lines inside gamma phase during creep, obeying an orientation relationship of [001]TiAl//[001]TiAl2, (020)TiAl//(200)TiAl2. Meanwhile, TiAl2 phase maintains a small planar disregistry of 1.54% with gamma matrix. With the increase of creep deformation or creep time, more TiAl2 phases gradually nucleate and grow.