Microstructural Characterization of Creep Cavitation in a Fully-Lamellar TiAl Alloy

XW Du,J Zhu,YW Kim
DOI: https://doi.org/10.1016/s0966-9795(00)00117-5
IF: 4.075
2001-01-01
Intermetallics
Abstract:Ti–46.5Al–2Cr–3Nb–0.2W with a fully-lamellar microstructure was crept under 1073 K, 270 MPa. Creep fracture is due to cavitation on grain boundaries. Cavity nucleation follows two mechanisms: dynamic recrystallization mechanism and interlocked mechanism. The two mechanisms suggest that, different from in polycrystalline materials, in fully-lamellar materials the difference of grain orientation determines the cavity nucleation at grain boundaries. Cavity shape and experimental data of cavity growth rate are in agreement with quasi-equilibrium growth theory, so proper alloy-doping and heat treatment can improve creep resistance by reducing diffusive conductance of the grain boundary.