Abstract:Ti-6.5Al-2Zr-1Mo-1V/TiB metal matrix composites with 3 wt.% of TiB2 were obtained using vacuum arc melting and spark plasma sintering methods and compared with an unreinforced Ti-6.5Al-2Zr-1Mo-1V alloy. The microstructures of the unreinforced Ti6.5Al-2Zr-1Mo-1V alloy in the as-cast and as-sintered conditions were quite typical and consisted of colonies of α-lamellae embedded in the β matrix. The microstructure of the as-cast Ti-6.5Al-2Zr-1Mo-1V/TiB composite composed of TiB fibers randomly distributed within the two-phase α/β matrix, while the as-sintered composite had a network-like microstructure, in which areas of the two-phase α/β matrix were delineated by walls of TiB fibers. At room temperature, the yield strength of the as-cast and as-sintered Ti-6.5Al-2Zr-1Mo-1V alloy were 800 and 915 MPa, respectively, with a plasticity of 18% in both conditions. The addition of TiB fibers contributed to a ~40 and 50% strength increment, with values of 1100 and 1370 MPa for the as-cast and as-sintered composites, respectively. In the as-sintered composite, the strengthening effect reduced at 400 °C and almost disappeared at elevated temperatures of 800–950 °C. The as-cast composite showed much higher strength during warm and hot deformation—at 800–950 °C, the yield strength of the as-cast composite was 50% higher compared to the Ti-6.5Al-2Zr-1Mo-1V unreinforced alloy. A higher rate and degree of globularization were established for the as-cast composite compared to the unreinforced alloy. For the as-sintered composite, a noticeably lower rate and degree of globularization was shown. During hot compression of the as-cast composite, TiB fibers reoriented towards the metal flow direction, while the network microstructure formed in the as-sintered composite transformed into clusters of borides unevenly distributed within the matrix. Based on the obtained results, the apparent activation energy of plastic deformation was calculated, and the operating deformation mechanisms were discussed both for the as-cast and as-sintered composites. The Arrhenius flow stress model and the dynamic material model were used to evaluate the deformation behavior of composites beyond the experimentally studied temperatures and strain rates.

Significantly Enhanced Creep Resistance of Low Volume Fraction In-Situ TiBw/Ti6Al4V Composites by Architectured Network Reinforcements

Constructing Two-Scale Network Microstructure with Nano-Ti5si3 for Superhigh Creep Resistance

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

IN SITU TiBW/Ti COMPOSITES WITH A NOVEL QUASI- CONTINUOUS NETWORK REINFORCEMENT ARCHITECTURE

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

Room temperature tensile fracture characteristics of in situ TiBw/Ti6Al4V composites with a quasi-continuous network architecture

In situ (TiBw+TiCp)/Ti6Al4V composites with a network reinforcement distribution

Tailoring A Novel Network Reinforcement Architecture Exploiting Superior Tensile Properties of in Situ Tibw/Ti Composites

Oxidation behavior of in situ TiCp/Ti6Al4V composite with self-assembled network microstructure fabricated by reaction hot pressing

Effect of In-Situ TiB2 Particles on the Creep Properties of 3 Wt.% TiB2/Al-Cu-Mg-Ag Composite

High temperature performance of TiB/(Ti-6.5Al-2Zr-1Mo-1V-0.5Si) composites affected by the TiB architecture

Short-time creep behavior of (TiB + TiC + Y2O3) reinforced titanium matrix composite in the range of 600 °C to 700 °C

The creep behavior of (TiB + TiC + Y2O3)/α-Ti composites at high temperature and short-term

Experimental verification and numerical analysis on plastic deformation and mechanical properties of the in-situ TiB2 homogeneous composites and TiB2/Cu network composites prepared by powder metallurgy

Enhanced creep resistance induced by minor Ti additions to a second generation nickel-based single crystal superalloy

Microstructure Evolution and Mechanical Behavior of TiB-Reinforced Ti-6.5Al-2Zr-1Mo-1V Matrix Composites Obtained by Vacuum Arc Melting and Spark Plasma Sintering

Network-Strengthened Ti-6Al-4V/(TiC+TiB) Composites: Powder Metallurgy Processing and Enhanced Tensile Properties at Elevated Temperatures

Differences in mechanical properties and high temperature deformation behavior between TiBw/Ti65 and TiBw/TA15 composites with network structure

Co-construction of microstructure evolution and wear resistance of in-situ TiBw/TA15 composites with network structure

Construction of Three-Dimensional Network Morphology Titanium Matrix Composites Via Adding Nano B4C: As-built and Heat-Treated Scenarios

Wear resistance enhancement mechanism of columnar network distributed TiBw in titanium matrix composites