Formative and controlled mechanisms of nano-sized γ′ precipitates with local phase-transition within dislocation networks of nickel-based single crystal superalloys

Wanshun Xia,Xinbao Zhao,Quanzhao Yue,Liang Yue,Jiangwei Wang,Qingqing Ding,Hongbin Bei,Ze Zhang
DOI: https://doi.org/10.1016/j.actamat.2021.116653
IF: 9.4
2021-03-01
Acta Materialia
Abstract:<p>The chemical and structural evolution within dislocation networks are investigated in a nickel-based single crystal superalloy crept under 1373K and 137MPa. The local region within dislocation networks can be divided to two separated parts: gridlines which compose the arrangements of dislocation networks and mesh regions as intervals between gridlines. With evolution of dislocation networks, precipitation of nano-sized γ′ phase (γ′<sub>n</sub>) are observed in mesh region, while gridlines always display the FCC feature of γ phase. The formative mechanism of γ′<sub>n</sub> is revealed as increased segregations of Cr, Co and Re along gridlines which enhance the contents of γ′-rich elements such as Al in mesh region to promote the local phase transition from FCC to highly ordered L1<sub>2</sub>. However, growth of γ′<sub>n</sub> requires massive diffusion of γ′-rich elements that is confined by the chemical barrier along gridlines with strong segregations of Cr, Co and Re. The mesh region of γ′<sub>n</sub> and gridlines of γ reinforce each other forming potential γ/γ′ substructures to stabilize the dislocation networks during creep. Denser dislocation networks formed in dendrite core under larger local lattice misfit are accompanied with facilitated formation of γ/γ′ substructures which derive higher creep resistance than interdendritic region.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?