The precipitation of η phase during the solution treatments of Allvac 718Plus

Liting Tang,Hongyu Zhang,Qianying Guo,Chenxi Liu,Chong Li,Yongchang Liu
DOI: https://doi.org/10.1016/j.matchar.2021.111142
IF: 4.537
2021-06-01
Materials Characterization
Abstract:<p>The precipitation of η phase during the solution treatments of Allvac 718Plus was investigated in this study. The results showed that there was free-γ′ zone appearing around η phase which was consistent with the hexagonal η-Ni<sub>3</sub>(Al/Ti)<sub>0.5</sub>Nb<sub>0.5</sub> after heat treatments. The granular η phase was found to be the transition of the plate-like η phase and have no pinning effect against the grain boundary, while the plate-like η phase has a pinning effect on the grain boundary and leads to the formation of serrated grain boundaries. With the solution temperature increasing, the size and fraction of η phase were observed to increase and then decrease with the morphology changing from granular to plate-like and then to granular. With the solution time prolonging, the fraction and size of η phase were increased, and the η phase formed in a cellular mode and then grow in a Widmanstätten morphology into the grain with its morphology changing from the dominant granular/plate-like to Widmanstättan structure. It was found that the increase in room temperature microhardness with the solution time changing from 6 h to 24 h was caused by the formation of Widmanstätten η phase.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
What problem does this paper attempt to address?