Influence of high altitude on the strength of aerated concrete

Biwen Liu,Qian Zhang,Yuxiang Zhao,Dongdong Huan,Xinzhong Liu

DOI: https://doi.org/10.1039/d2ra06498g

IF: 4.036

2023-01-01

RSC Advances

Abstract:The specimens prepared with different temperature have different content and crystallinity of tobermorite, resulting in different strength.

chemistry, multidisciplinary

What problem does this paper attempt to address?

Experimental study on dynamic behavior of concrete at elevated temperatures

Yuanming He,Jingsi Huo,Yan Xiao

DOI: https://doi.org/10.1166/asl.2011.1732

2011-01-01

Advanced Science Letters

Abstract:A split Hopkinson pressure bar (SHPB) was used experimentally to investigate the dynamic behavior of concrete at elevated temperatures. After the cylinder concrete specimens were heated to a pre-determined temperature by a purpose-developed electrical furnace, they were impacted by the SHPB bars to failure. The stress and strain time history curves of the tested specimens were recorded to analyze the impact behavior of concrete at elevated temperatures. The effects of high temperature and impact velocity on the dynamic strength and stress versus strain relationships of concrete were discussed. Generally, the dynamic strength of concrete at elevated temperatures decreased while the compressive deformation increased remarkably with the increase of temperature. Concrete at elevated temperatures tended to be more strain-rate sensitive under impact loading with the increase of high temperature except that at temperature of 200 degrees C. The dynamic behavior of concrete at temperature of 200 degrees C was obviously different from that of concrete specimens at room temperature and at elevated temperatures higher than 200 degrees C. Therefore, much attention should be paid to no dynamic effect of concrete at temperature of 200 degrees C.
Finite element analysis of temperature effect and crack-control measures for ultra-long concrete structures

ZHU Haochuan,XIAO Zhibin,SHAO Jianwen,TONG Genshu

DOI: https://doi.org/10.19701/j.jzjg.ls202114

2023-01-01

Abstract:Temperature stress is the main problem faced by ultra-long concrete structure, how to accurately simulate the structural temperature effect and take effective measures to control the crack generation is the key to deal with this kind of problem. Based on the finite element analysis and practical engineering application of ultra-long concrete structures, the calculation method of structural temperature difference and the determination principle of key parameters were proposed, and a new method of crack-control was also introduced. The analysis shows that the finite element modeling can reveal temperature variation effect effectively and reasonably. The proposing floor elevation zone can weaken the impact of temperature stress, and avoid ultra-long concrete structure cracking.
EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

ZHENG Qiu,HUO Jing-si,CHEN Bai-sheng,XIAO Yan

2009-01-01

Abstract:The impact behavior of 15 concrete-filled steel tubes(CFT) specimens under different temperatures ranging from room temperature to 400℃ was experimentally studied using a spilt Hopkinson pressure bar(SHPB).The stress and strain time history curves of the tested specimens were recorded to analyze the impact behavior of CFT under high temperatures.The failure patterns and the recorded load versus deformation curves demonstrate that the CFT has an excellent impact-resistant behavior under high temperatures,i.e.relatively higher strength and post-yielding strength,excellent plasticity and integrity of the composite section.
Microstructures and Properties of Concrete Surfaces under Different Exposure Conditions in Complex Natural Environments of High-Altitude Regions

Xin Chen,Xu Liu,Yongrui Feng,Xin Huang,Lihui Li,Yong Ge,Bo Tian

DOI: https://doi.org/10.1016/j.jobe.2023.106663

IF: 7.144

2023-01-01

Journal of Building Engineering

Abstract:The quality of concrete surfaces is negatively affected by the plateau climate. The purpose of present study was to investigate the mechanism of the climate effect on the microstructures and properties of concrete surfaces under different exposure conditions. Scanning electron micro-scopy, X-ray diffraction, thermogravimetry, nitrogen adsorption porosimetry, mercury intrusion porosimetry, and microhardness tests were used for microstructure analysis. Rebound strength and abrasion resistance tests were conducted to assess the mechanical properties. Tests of sorp-tivity under various absorption conditions, chloride ion impenetrability after vacuum saturation and immersion, and deicing salt scaling with natural and standard freeze-thaw cycling, were conducted to assess the durability. The results showed that both cement hydration and micro-structure densification of the exposed concrete surfaces were lower than those of the concrete interior, leading to worse mechanical properties and durability. The rapid moisture loss, rather than the low temperature, was the dominant cause of the weak surface layer, with a depth be-tween 10 mm and 15 mm. The performance of a south-oriented surface was slightly better than that of a north-oriented surface, which was due to the stronger solar radiation for the former surface. However, the difference was so small that it could be ignored. Furthermore, the concrete sorptivity under the conditions of semi-immersion and vacuum saturation was lower in the high-altitude regions, which was due to the higher evaporation and smaller pressure difference after vacuum absorption. Thus, significant errors were expected in all tests of chloride ion impene-trability assessment conducted in high-altitude regions.
Effect of Temperature on Pore Structure and Strength of Concrete

Jiarong Shen,Qianjun Xu,Qingbin Li

DOI: https://doi.org/10.14359/51718060

2019-01-01

ACI Materials Journal

Abstract:The aim of this study is to quantitatively determine the effect of elevated temperatures on the pore structure and compressive strength of concrete. To minimize the effect of the hydration process, thermal and endogenous shrinkage, concrete cured in water for 12 months was tested. Evolutions of pore structure under elevated temperatures (40, 105, 150, 200, and 250 degrees C [104, 221, 302, 392 and 482 degrees R) were characterized by mercury intrusion porosimetry (MIP), N-2 adsorption, and scanning electron microscope (SEM) tests. Compressive strength tests were carried out to characterize the mechanical properties. The experimental results showed that with the increase of temperature, the porosity increased and the pore structure destroyed gradually. The changes in porosity and pore structure can be explained by the loss of water in concrete. In addition, the compressive strength decreased with increasing temperature. The relationship between compressive strength and porosity after heating at elevated temperatures fitted well with the strength-porosity logarithmic relation proposed by Schiller: The correlation coefficient is 0.994, which indicated that the effect of elevated temperature on the compressive strength of concrete can be quantitatively determined by Schiller function.
Simulation Analysis of Pumping Characteristics for High-Altitude Concrete

Guoju Ke,Bo Tian,Yangtao Yuan,Jun Zhang,Lihui Li

DOI: https://doi.org/10.1061/(ASCE)MT.1943-5533.0004002

IF: 3.2

2022-01-01

Journal of Materials in Civil Engineering

Abstract:To investigate the characteristics of high-altitude concrete, the influences of atmospheric pressure on the air content, bubble stability, and pore structure of air-entrained concrete were tested by simulating a low-pressure condition using an environmental chamber. The pumping process was simulated using a resistance tester to investigate the effects of atmospheric pressure on the concrete slump, slump flow, V-funnel time, and pumping resistance. The results showed that the air content of air-entrained concrete decreases significantly with decreasing atmospheric pressure and that the pore structure of hardened concrete deteriorates. Among the admixture components, the effect of the air-entraining agent (AEA) on reducing concrete pumping resistance was the most evident. The pumping resistance of concrete increases at low atmospheric pressure, but that of concrete with AEA increases minimally. Combined with the ideal gas state equation, the air-entraining mechanism of high-altitude concrete was explained.
Experimental research on strength decaying of concrete with different grades at elevated temperature

Xiao Minghui,Shi Xudong,Xing Wanli

2009-01-01

Abstract:Through high temperature experiments of concrete with different strength grades and water cement ratios,the effect of these influencing factors on its strength decaying was examined.From the test results it is shown that the concrete strength does not monotonously decline with increase in action temperature and experiences three successive phases: declining at low temperature,recovery and decaying at high temperature.But there still exists a similar trend for different strength grade concretes and has a minimal value at about 200℃.
Experimental study on compressive strength of concrete under lasting sub-high temperature

Shi Xudong,Liu Chao,Li Liang,Xing Wanli

2011-01-01

Abstract:Existing researches on behaviors of heated concrete are mainly focused on the high temperature range above 500℃.The compressive strength of concrete under sub-high temperature(<500℃) is only simply taken as that at room temperature,and this does not accord with its actual mechanical properties.It is more important to investigate the mechanical properties of concrete in the structures subjected to long-term sub-high temperature.The influences of sub-high temperature and its lasting time on the concrete compressive strength were investigated based on experiments.It is shown that the concrete compressive strength with different temperature lasting time has a similar changing trend.There exists a strength fluctuation from 100℃ to 250℃ with a concave around 100℃ and sharp decrease after 250℃.Temperature lasting time has little effect on the compressive strength after the temperature distribution becomes uniform.A calculation formula of strength of concrete subjected to sub-high temperature was presented.
Study on the preparation and performances analysis of lightweight high strength ceramsite aerated concrete

Peng Liu,Ao Luo,Lei Liu,Yongling Li,Sanling Zhang,Weiting Zhi,Dong Pan,Ying Chen,Zhiwu Yu

DOI: https://doi.org/10.1016/j.jmrt.2023.07.076

IF: 6.267

2023-07-15

Journal of Materials Research and Technology

Abstract:An orthogonal test of the component design of aerated concrete was carried out to solve the problems of low strength, easy cracking, and high water absorption of aerated concrete. The influences of cement content, water-binder ratio, foaming agent content, and polypropylene fiber content on the performances of aerated concrete including dry density, compressive strength, and thermal conductivity were investigated. Furthermore, the optimal composition of aerated concrete was determined. The test results showed that the dry density, compressive strength, thermal conductivity, and water absorption of aerated concrete were greatly influenced by the dosage of the foaming agent. Additionally, the water-binder ratio was found to significantly influence the apparent porosity of aerated concrete. Based on the experiment, the optimal combination of components for aerated concrete was 65 wt.% cement and 35% wt.% mineral admixture with a fly ash to slag ratio of 3:1. Meanwhile, the content of water-binder ratio, foaming agent, and polypropylene fibers were 0.4, 4 wt.%, and 0.4 wt.% of the total cementitious material, respectively. Among the mix proportions in this study, aerated concrete prepared by using the above mix proportion had the best performances. Subsequently, the influence of ceramsite content on the strength, dry density, and thermal conductivity of aerated concrete was analyzed. The results showed that the dry density and thermal conductivity of ceramiste aerated concrete increased with the increase of ceramsite content, but the change law of the water absorption was the opposite. Moreover, the compressive strength increased first and then decreased with the increase of ceramsite content, while the apparent porosity was the opposite. The optimal ceramsite content in ceramsite aerated concrete was 20 wt.%.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Effect of Thermal Environment at Early Age on Hydration Phases Composition and Strength Development of Concrete Containing Fly Ash

Fengchen Zhang,Dejian Shen,Jikai Zhou,Zhonghua Li

DOI: https://doi.org/10.4028/www.scientific.net/amr.168-170.582

2010-01-01

Advanced Materials Research

Abstract:Cement hydration at early age is sometimes in a certain thermal environment probably caused by hydration heat of mass concrete as well as cement productions curing at high temperature. And phases composition and strength development in thermal environment are commonly different from those in normal curing conditions. Phases composition and strength development of concrete containing different fly ash content curing in different thermal environment are studied in this paper. Experimental results show that compressive strengths of concrete with 0.3 water to binder ratio increase with the increase of curing temperature. Splitting tensile strength of concrete not containing any fly ash curing at about 50 is the highest among those curing at temperature between 40 and 80 . For concrete with different fly ash content, splitting tensile strengths increase approximately with the increse of curing temperature. Dehydration of ettringite and formation of monosulfate solid solution and AFm at higher temperature perhaps relate to the development of concrete splitting tensile strength along with different curing temperature. Adding fly ash to binder, curing temperature at which hydration phases change occurs is raised, which helps to explain that splitting tensile strengths of concrete with different fly ash content decrease little with the increase of curing temperature between 60 and 80 .
Influence of air-entraining agent and freeze-thaw action on pore structure in high-strength concrete by using CT-Scan technology

Dorys C. González,Álvaro Mena,Jesús Mínguez,Miguel A. Vicente

DOI: https://doi.org/10.1016/j.coldregions.2021.103397

IF: 4.427

2021-12-01

Cold Regions Science and Technology

Abstract:In this work, the effects caused by both the amount of air-entraining agent (AEA) and freeze-thaw cycles on microstructure of high-strength concrete have been analyzed. For this purpose, five series of concrete specimens have been manufactured, each of them containing a different amount of AEA. Then, all series have been subjected to up to 300 freeze-thaw cycles. In addition, the specimens have been analyzed using a computed tomography (CT) scan device at pre-defined freeze-thaw cycles and all data have been processed with digital image processing (DIP) software.The results reveal, on the one hand, that the quantity of AEA has a greater influence on pore structure, and additionally the freeze-thaw action only slightly modifies the pore structure. As AEA increases, a progressive rise of the porosity and the number of pores is observed up to a maximum value. Next, a decrease is noticed. Moreover, there is not a linear relation between porosity and AEA. Furthermore, as AEA increases, a variation of its size and shape is observed. Alternatively, the effect of freeze-thaw cycles is more complex and does not show a monotonous tendency. The results reveal that the first 50 freeze-thaw cycles have the strongest influence on pore structure, observing a decrease in porosity. For the rest of the cycles, the porosity increases progressively resulting, after 300 freeze-thaw cycles, in a slightly lower porosity in almost all series than in those presented at the beginning. Hydration of unhydrated cement particles alongside with microcracking act as opposite performances during the freeze-thaw cycles. Therefore, this can suggest that, under these conditions, freeze-thaw action is not able to damage significantly the microstructure of concrete.The results show that the series with a lower AEA content show a better behavior under freeze-thaw cycles. In this case, the specimens exhibit a lower porosity and a higher level of small pores, and the pores evince a more elongated shape. All these features lead to a more impermeable concrete and, therefore, with a better performance under freeze-thaw cycles.

engineering, environmental, civil,geosciences, multidisciplinary
Study on concrete at high temperature in China—an overview

Jianzhuang Xiao,Gert König

DOI: https://doi.org/10.1016/s0379-7112(03)00093-6

IF: 3.78

2004-02-01

Fire Safety Journal

Abstract:Based on the investigation and review of experimental studies in the past 20 years in the People's Republic of China, this paper engages in further discussion and comparative analysis of researches on the mechanical behavior of concrete both under and after high temperature exposure. The following three aspects are focused on. First, the basic mechanical behavior of concrete at high temperature, including strength, elastic modulus, peak strain and Poisson's ratio. Second, the effect of high temperature on the yield strength and elastic modulus of rebar. And last but not the least, the high temperature response to the bond behavior between concrete and rebar. This overview summaries the states-of-the-art studies on the mechanical behavior of concrete at high temperature in China.

materials science, multidisciplinary,engineering, civil
Influence of Initial Curing Temperature on the Long-Term Strength of Concrete

Runxiao Zhang,Nannan Shi,Dahai Huang

DOI: https://doi.org/10.1680/macr.12.00107

IF: 2.46

2013-01-01

Magazine of Concrete Research

Abstract:The growth of concrete strength is markedly influenced by curing temperature and age. In this paper, the reason why final strength difference occurs between concrete cured under various isothermal temperatures is analysed from a microreaction mechanism angle. Based on an available long-term strength predicting model, a modified model is proposed that could quantify the initial temperature's impact on the long-term and limiting strength. Moreover, experimental data available in the literature are collected and utilised to regress and confirm the parameter value in this new model. The results of analysis for the model indicate that the initial 4 h temperature determines concrete's final strength if neglecting other non-temperature factors.
Physical Properties and Hydration Characteristics of Low-Heat Portland Cement at High-Altitude

Ning Wang,Qiang Liu,Yanqing Xia,Jun Li,Zhongyuan Lu,Yigang Xu,Wen Zhong,Yan Lin

DOI: https://doi.org/10.3390/ma16083110

IF: 3.4

2023-04-15

Materials

Abstract:High-altitude environments are characterized by low air pressures and temperature variations. Low-heat Portland cement (PLH) is a more energy-efficient alternative to ordinary Portland cement (OPC); however, the hydration properties of PLH at high altitudes have not been previously investigated. Therefore, in this study, the mechanical strengths and levels of the drying shrinkage of PLH mortars under standard, low-air-pressure (LP), and low-air-pressure and variable-temperature (LPT) conditions were evaluated and compared. In addition, the hydration characteristics, pore size distributions, and C-S-H Ca/Si ratio of the PLH pastes under different curing conditions were explored using X-ray diffraction (XRD), thermogravimetric analysis (TG), scanning electron microscopy (SEM), and mercury intrusion porosimetry (MIP). Compared with that of the PLH mortar cured under the standard conditions, the compressive strength of the PLH mortar cured under the LPT conditions was higher at an early curing stage but lower at a later curing stage. In addition, drying shrinkage under the LPT conditions developed rapidly at an early stage but slowly at a later stage. Moreover, the characteristic peaks of ettringite (AFt) were not observed in the XRD pattern after curing for 28 d, and AFt transformed into AFm under the LPT conditions. The pore size distribution characteristics of the specimens cured under the LPT conditions deteriorated, which was related to water evaporation and micro-crack formation at low air pressures. The low pressure hindered the reaction between belite and water, which contributed to a significant change in the C-S-H Ca/Si ratio in the early curing stage in the LPT environment.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
Effect of Low Temperature on Mechanical Properties of Concrete with Different Strength Grade

Xiaoping Cai,Wencui Yang,Jie Yuan,Yong Ge,Baosheng Zhang

DOI: https://doi.org/10.4028/www.scientific.net/kem.477.308

2011-01-01

Key Engineering Materials

Abstract:The effect of low temperature (-35°C) on the mechanical properties of concrete with different strength grade such as compressive strength, flexural strength, splitting tensile strength and elastic modulus was studied. The results showed that all of the mechanical properties were improved at -35°C. It was also can be found from the tests, as the strength grade increased, the growth ratios at -35°C of compressive strength, flexural strength and splitting tensile strength decreased. But the growth ratio of elastic modulus increased with the increasing of strength grade.
Thermal Resistance, Water Absorption and Microstructure of High-Strength Self-Compacting Lightweight Aggregate Concrete (HSSC-LWAC) after Exposure to Elevated Temperatures

Jiuwen Bao,Rui Zheng,Peng Zhang,Yifei Cui,Shanbin Xue,Qiang Song,Yanxuan Ma

DOI: https://doi.org/10.1016/j.conbuildmat.2022.130071

2023-01-01

Abstract:An experimental investigation on the influence of elevated temperatures on the thermal resistance, water absorption and microstructure of high-strength self-compacting lightweight aggregate concrete (HSSC-LWAC) is presented. In total, 315 concrete specimens from 7 different mixtures with different replacement ratios (0, 30 %, 50 % and 100 % by weight) of two kinds of LWAs, namely cloud concrete stone (CCS) and fly ash ceramsite (FAC), were prepared. The workability of fresh concrete mixtures including slump, J-Ring and T500 tests was first conducted aiming at meeting the requirements of self-compacting performance. Hardened concrete specimens were then exposed to different elevated temperatures (i.e. 200 degrees C, 400 degrees C, 600 degrees C and 800 degrees C) increased with a heating rate of 10 degrees C/min. A series of tests including the apparent morphology, ultrasound pulse velocity (UPV), residual compressive strength and capillary water absorption were carried out on unheated control concrete and after air-cooling period of heated concrete. Finally, the thermal analysis and microstructural observation were further conducted through the thermogravimetry (TG), differential scanning calorimetry (DSC), mercury intrusion porosimetry (MIP), laser scanning microscopy (LSM) and scanning electron microscope (SEM) to characterize the evolution of high temperature damage. Generally, the high temperature resistance of HSSCLWAC shows an increasing trend as the LWAs content increases, while the residual mechanical strength increases and then decreases with an increase of the temperature gradient. The microstructural observation indicates that the evolution behavior of thermal damage promotes the continuous development of micropores in the interfacial transition zones (ITZ) to form wider microcracks, resulting in the degradation of residual mechanical properties.
Comparison between high strength concrete and normal strength concrete subjected to high temperature

Sammy Y. N. Chan,Gai-fei Peng,John K. W. Chan

DOI: https://doi.org/10.1007/bf02485969

1996-12-01

Materials and Structures

Abstract:Two normal strength concretes and three high strength concretes, with 28-day compressive strengths of 28, 47, 76, 79 and 94 MPa respectively, were used to compare the effect of high temperatures on high strength concrete and normal strength concrete. After being heated to a series of maximum temperatures at 400, 600, 800, 1000 and 1200°C, and maintained for 1 hour, their compressive strengths and tensile splitting strengths were determined. The pore size distribution of hardened cement paste in high strength concrete and normal strength concrete was also investigated. Results show that high strength concrete lost its mechanical strength in a manner similar to or slightly better than that of NSC. The range between 400 and 800°C was critical to the strength loss of concrete with a large percentage of loss of strength. Microstructural study carried out revealed that high temperatures have a coarsening effect on the microstructure of both of high strength concrete and normal strength concrete.

construction & building technology,materials science, multidisciplinary,engineering, civil
Effects of Curing Regimes on Strength Development of High-Strength Concrete

Peiyu YAN,Qiang CUI

DOI: https://doi.org/10.14062/j.issn.0454-5648.2015.02.01

2015-01-01

Abstract:The effect of three curing regimes of standard condition (20℃、relative humidity≥90%), elevated temperature of 50℃and temperature match condition on compressive strength development of high-strength concrete. Results show that elevating curing temperature higher than 50℃ can significantly increase the activity of composite binders consisting of cement-ground granular blast furnace slag(GGBS) and cement-fly ash-silica fume. The compressive strength of concrete prepared with these composite binders and cured at elevated temperature is twice of that cured in the standard condition in 3 d age and continues to grow in long age. The elevated temperature curing regime restrains the compressive strength development of concrete prepared with only Portland cement in long age. Strength of concrete increases greatly when the hydration of binder goes intensively in the stage of nucleation and crystal growth or interaction at phase boundaries. The increasing extent for strength of concrete and its difference among concretes declines when the hydration of binder goes into the stage of diffusion. Concrete prepared with cement-fly ash-silica fume composite binder cured in any regime has the highest strength and the best resistance to chloride ion penetration. This composite binder is suitable for the preparation of high-strength concrete. The strength determined using a sample cured under the standard condition can approximately reflect the property of concrete in real structure for long term.
Effect of High Temperature on Residual Mechanical Properties of Confined and Unconfined High-Strength Concrete

B Wu,XP Su,H Li,J Yuan

DOI: https://doi.org/10.14359/12223

2002-01-01

ACI Materials Journal

Abstract:With the increasing use of high-strength concrete (f(c) > 60 MPa) in building construction, the risk of exposing these structures to high temperatures during afire has increased significantly. To be able to assess the structural safety of such structures after a fire, it is important that the mechanical properties of the material be well assessed with regard to high-temperature effects. In this context, a study was conducted to investigate the residual mechanical properties of confined and unconfined high-strength concrete (f(c) = 70 MPa) after a single thermal cycle at 100, 200, 300, 400, 500, 600, 700, 800, and 900 degreesC An analytical model for the stress-strain relationship for uniaxially loaded high-strength concrete was empirically developed and was shown to be applicable to confined and unconfined concrete after a cycle at a high temperature. The main parameters required to establish the stress-strain relationship are the peak stress, the elastic modulus, and the strain at peak stress. Empirical expressions for these parameters were dei eloped to take into account the temperature and the level of confinement. The knowledge of the residual mechanical properties of concrete is necessary whenever the thermally damaged structure is required to bear a significant share of the loads, even after a severe thermal accident.
Effects of Nano-Caco3 on the Compressive Strength and Microstructure of High Strength Concrete in Different Curing Temperature

Qinglei Xu,Tao Meng,Miaozhou Huang

DOI: https://doi.org/10.4028/www.scientific.net/amm.121-126.126

2011-01-01

Applied Mechanics and Materials

Abstract:In this paper, effects of nano-CaCO3 on compressive strength and Microstructure of high strength concrete in standard curing temperature(21±1°C) and low curing temperature(6.5±1°C) was studied. In order to improve the early strength of the concrete in low temperature, the early strength agent calcium nitrite was added into. Test results indicated that 0.5% dosage of nano-CaCO3 could inhibit the effect of calcium nitrite as early strength agent, but 1% and 2% dosage of nano-CaCO3 could improve the strength of the concrete by 13% and 18% in standard curing temperature and by 17% and 14% in low curing temperature at the age of 3days. According to the XRD spectrum, with the dosage up to 1% to 2%, nano-CaCO3 can change the orientation index significantly, leading to the improvement of strength of concrete both in standard curing temperature and low curing temperature.

Influence of high altitude on the strength of aerated concrete

Experimental study on dynamic behavior of concrete at elevated temperatures

Finite element analysis of temperature effect and crack-control measures for ultra-long concrete structures

EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

Microstructures and Properties of Concrete Surfaces under Different Exposure Conditions in Complex Natural Environments of High-Altitude Regions

Effect of Temperature on Pore Structure and Strength of Concrete

Simulation Analysis of Pumping Characteristics for High-Altitude Concrete

Experimental research on strength decaying of concrete with different grades at elevated temperature

Experimental study on compressive strength of concrete under lasting sub-high temperature

Study on the preparation and performances analysis of lightweight high strength ceramsite aerated concrete

Effect of Thermal Environment at Early Age on Hydration Phases Composition and Strength Development of Concrete Containing Fly Ash

Influence of air-entraining agent and freeze-thaw action on pore structure in high-strength concrete by using CT-Scan technology

Study on concrete at high temperature in China—an overview

Influence of Initial Curing Temperature on the Long-Term Strength of Concrete

Physical Properties and Hydration Characteristics of Low-Heat Portland Cement at High-Altitude

Effect of Low Temperature on Mechanical Properties of Concrete with Different Strength Grade

Thermal Resistance, Water Absorption and Microstructure of High-Strength Self-Compacting Lightweight Aggregate Concrete (HSSC-LWAC) after Exposure to Elevated Temperatures

Comparison between high strength concrete and normal strength concrete subjected to high temperature

Effects of Curing Regimes on Strength Development of High-Strength Concrete

Effect of High Temperature on Residual Mechanical Properties of Confined and Unconfined High-Strength Concrete

Effects of Nano-Caco3 on the Compressive Strength and Microstructure of High Strength Concrete in Different Curing Temperature