Abstract:High-altitude environments are characterized by low air pressures and temperature variations. Low-heat Portland cement (PLH) is a more energy-efficient alternative to ordinary Portland cement (OPC); however, the hydration properties of PLH at high altitudes have not been previously investigated. Therefore, in this study, the mechanical strengths and levels of the drying shrinkage of PLH mortars under standard, low-air-pressure (LP), and low-air-pressure and variable-temperature (LPT) conditions were evaluated and compared. In addition, the hydration characteristics, pore size distributions, and C-S-H Ca/Si ratio of the PLH pastes under different curing conditions were explored using X-ray diffraction (XRD), thermogravimetric analysis (TG), scanning electron microscopy (SEM), and mercury intrusion porosimetry (MIP). Compared with that of the PLH mortar cured under the standard conditions, the compressive strength of the PLH mortar cured under the LPT conditions was higher at an early curing stage but lower at a later curing stage. In addition, drying shrinkage under the LPT conditions developed rapidly at an early stage but slowly at a later stage. Moreover, the characteristic peaks of ettringite (AFt) were not observed in the XRD pattern after curing for 28 d, and AFt transformed into AFm under the LPT conditions. The pore size distribution characteristics of the specimens cured under the LPT conditions deteriorated, which was related to water evaporation and micro-crack formation at low air pressures. The low pressure hindered the reaction between belite and water, which contributed to a significant change in the C-S-H Ca/Si ratio in the early curing stage in the LPT environment.

What problem does this paper attempt to address?

The paper attempts to address the hydration characteristics and physical properties of low-heat Portland cement (PLH) in high-altitude environments. Specifically, the study aims to explore the effects of low air pressure and temperature variations on the mechanical strength, drying shrinkage, hydration characteristics, pore distribution, and C-S-H Ca/Si ratio of PLH, thereby providing scientific evidence for its application in high-altitude environments. ### Background and Issues 1. **Characteristics of High-Altitude Environments**: - Low air pressure - Large temperature variations 2. **Problems of Ordinary Portland Cement (OPC) in High-Altitude Environments**: - Hydration characteristics are affected - Compressive strength and durability are reduced - Engineering lifespan is impacted 3. **Advantages of Low-Heat Portland Cement (PLH)**: - Contains high belite content (C2S) - Theoretical low energy consumption - Low early hydration heat - Helps reduce early cracking and drying shrinkage of concrete 4. **Necessity of the Study**: - Increased infrastructure construction in high-altitude areas - Hydration characteristics of low-heat Portland cement in these environments have not been studied ### Research Objectives - **Evaluate the mechanical properties of PLH under different curing conditions**: - Standard conditions - Low air pressure conditions (LP) - Low air pressure and temperature variation conditions (LPT) - **Analyze the drying shrinkage characteristics of PLH under different curing conditions** - **Explore the hydration characteristics of PLH under different curing conditions**: - X-ray diffraction (XRD) - Thermogravimetric analysis (TG) - Scanning electron microscopy (SEM) - Mercury intrusion porosimetry (MIP) - **Study the pore distribution and C-S-H Ca/Si ratio of PLH under different curing conditions** Through these studies, the authors hope to provide scientific evidence for the application of low-heat Portland cement in high-altitude environments, thereby improving its engineering performance and durability in these areas.

Physical Properties and Hydration Characteristics of Low-Heat Portland Cement at High-Altitude

Long-term Thermal Performance of Oil Well Cement Modified by Silica Flour with Different Particle Sizes in HTHP Environment

Study on the Strength and Hydration Behavior of Sulfate-Resistant Cement in High Geothermal Environment

How Competitive Hydration between C 3 A and C 3 S in the Fast Dissolution Stage Affects the Hydration of Low-Heat Portland Cement Blended Pastes

Hydration and Fractal Analysis on Low-Heat Portland Cement Pastes Using Thermodynamics-Based Methods

Effects of Tuff Powder on the Hydration Properties of Cement-Based Materials under High Temperature

Strength and Expansion of LHEC with Different Gypsum Contents under Thermal Curing

Investigation on the Unusual Hydration and Hardening Process of a Portland Cement with Low Alkali Sulfate Content

Study on Mechanical and Microscopic Properties of Fly Ash Cement-Based Materials in High Geothermal Environment

Hydration Mechanism and Mechanical-Thermal Correlation of Cemented Paste Backfill under Different Curing Temperatures

Low-Alite Portland Cement in Steam-Curing Condition: Long-Term Compressive Strength and Permeability

Effect of Curing Temperature on Mechanical Strength and Thermal Properties of Hydraulic Limestone Powder Concrete

Effect of n-C-S-H on Hydration and Reinforcement of Mineral Powder-Cement System at Low Temperatures

Experimental study of pure Class G cement hydration up to 150oC and 50MPa

Chloride Binding Behavior and Pore Structure Characteristics of Low-Calcium High-Strength Cement Pastes

Comparison of the Hydration Characteristics of UltraHighPerformance and Normal Cementitious Materials

Influence of Binder Types and Temperatures on the Mechanical Properties and Microstructure of Cemented Paste Backfill

Properties of High-Volume Limestone Powder Concrete under Standard Curing and Steam-Curing Conditions

Graphite-reinforced Portland cement composites at alternate ultra-high temperatures

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers

Effect of nanomaterials on the mechanical properties and microstructure of cement mortar under low air pressure curing